UV Resistant Properties of Composite Modiifed Nano Titanium Dioxide and Its Application
Xueyan Ma,Gang Wang,Guijun Yang,Huiyuan Chen,Xiaosong Li,Hong Lin
DOI: https://doi.org/10.3969/j.issn.1001-3539.2017.01.020
2017-01-01
Abstract:Surface of nanometer titanium dioxide (nano-TiO2) was modified by silane coupling agent (KH570) and compound modifiers of KH570 with organics [sorbitol,oleic acid,titanium acid ester,polyethylene glycol 6000 (PEG6000)]. The influences of coupling agent and different compound modifiers on the anti-ultraviolet capability of nano-TiO2 were studied. The nano-TiO2 before and after modified was characterized by scan electron microscope,secondary particle size analysis,the sedimentation test,fourier transform infrared spectroscopy,simultaneous thermal analysis. The results show that the nano-TiO2 modified by compound modi-fier KH570+PEG6000 has a minimum secondary particle size,and the average particle size is 0.047 μm,the absorbance of its supernate at sedimentation experiment is up to the highest of 1.067 76 at 350 nm,its oil absorption value is up to the maximum of 86.19 cm3/g,and the dispersibility and hydrophobicity are good. In addition,the nano-TiO2 modified by KH570+PEG6000 has the strongest ultraviolet absorption ability,and the lowest degradation rate to methylene blue solution. The PVC films were made through adding the modified nano-TiO2 into the poly(vinyl chloride) (PVC) matrix. The UV transmittance of those PVC films were received by accelerated aging for 120 h. It showes that the PVC films with nano-TiO2 modified by KH570+PEG6000 has a relatively lowest UV transmittance and highest tensile properties,which presents relatively superior resistance to ultraviolet and relatively ex-cellent modification effects of KH570+PEG6000.