Abstract:Nickel ferrite (NiFe2O4) nanoparticles were synthesized via solid-state reaction. The precursors obtained by grinding the mixture of FeSO4·7H2O, NiSO4·6H2O, NaOH and dispersant (NaCl) sufficiently at room temperature were calcined under various synthetic conditions in order to get NiFe2O4 spinel nanoparticles. The effects of the synthetic parameters, namely preparation technique, dispersant content, calcination temperature and heat preservation time, on particle size and morphology have been investigated in detail to find the optimized parameters. X-ray diffraction (XRD), thermogravimetry (TG) and differential thermal analysis (DTA), transmission electron microscopy (TEM) and vibrating sample magnetometer (VSM) were employed to characterize the precursors and as-synthesized particles. The results indicate that structural morphology varies between needle and sphere with changing preparation technique. Proper content of NaCl as a dispersant is beneficial to obtain uniform particles with a narrow size distribution. The particle morphology changes gradually from sphere to polygon with the increase in calcination temperature. Grain growth is enhanced by prolonging heat preservation time. Room temperature magnetization results reveal a ferromagnetic behavior of the as-synthesized NiFe2O4 nanoparticles. The saturation magnetization is enhanced with the increase in grain size for less surface effect. The coercivity is decreased for larger grain size because of magnetization reversal. The solid-state reaction technique is considered to be a convenient, inexpensive and effective preparation method of NiFe2O4 in high yield.

Nanocrystalline Spinel NiFe2O4 Synthesis by Solid-state Reaction at Low Heat

Synthesis of NiFe2O4 Spinel Nanopowder Via Low-Temperature Solid-State Reactions

Synthesis of Nanocrystalline(Ni_(0.58)Cu_(0.2)Zn_(0.22))Fe_(1.96)O_4 by Low-heating Solid-state Reaction

Research On Preparation And Characterization Of Nife2o4 Spinel Nanopowder Through Solid-State Reactions

Solid-state reaction synthesis of NiFe 2O 4 nanoparticles by optimizing the synthetic conditions

Preparation of Nanocrystalline LiMn1.90Cr0.05Ni0.05O4

Synthesis of Ni_0.6 Cu_0.2 Zn_0.2 Fe_2O_4 via Solid State Reaction at Low Heating Temperatures

Effects of Calcination Conditions on Particle Size and Morphology of NiFe 2 O 4 Nanoparticles Synthesized by Solid‐State Reaction

Synthesis, Structure and Magnetic Properties of Spinel Ferrite (ni, Cu, Co) Fe2O4 from Low Nickel Matte

Nanocrystalline ZnNiFeO

Co0.35Mn0.65Fe2O4 Magnetic Particles: Preparation and Kinetics Research of Thermal Process of the Precursor

Low Temperature Synthesis of LiNi0.5Mn1.5O4 Spinel

Synthesis of Ni-Zn Ferrite and Its Microstructure and Magnetic Properties

Solid State Synthesis of NiFe_2O_4 Nanoparticles at Low Temperature

Nanocrystalline Zn0.5Ni0.5Fe2O 4: Preparation and kinetics of thermal process of precursor

Effect of temperature schedule on the particle size of NiFe 2O4 spinel nanopowder during solid-state reactions

Solid State Reaction Synthesis of Ni(1-x)ZnxFe2O4 Spinel Used As Matrix of Inert Anodes in Aluminium Electrolysis

Synthesis of Nanocrystalline Spinel CoFe2O4 Via a Polymer-Pyrolysis Route

Synthesis and Characterization of NiFe<sub>2</sub>O<sub>4</sub>Nanoparticles via Solid-State Reaction

Low Temperature Route to Nanocrystalline LiMn2O4 Spinel

Magnetic Properties and Crystallization Kinetics of Zn0.5ni0.5fe2o4