Abstract:In this work, an improved wet bonding method was developed for strengthening of fiber-reinforced polymer. A self-made roughened carbon fiber–reinforced polymer sheet (hereinafter referred to as RFRP sheet) was externally attached to the surface layer of a nano-kaolin-modified concrete test piece to form an RFRP–concrete wet-bonded test piece. Then, the pull-off bond test and the single shear test were performed on 32 and 30 test pieces, respectively. The performance of the wet bonding interface of RFRP–concrete in the normal and tangential directions was investigated by changing the length of glass fiber cellosilk in RFRP bonding resin, the diameter of RFRP porous pelelith rock, and the ratio of nano-kaolin. In addition, by comparing the scanning electron microscopy images of untreated fiber-reinforced polymer sheet and the concrete block without nano-kaolin, the mechanism of the adhesion enhancement of the RFRP–concrete interface was explained. The results show that the differentiation between fiber-reinforced polymer–concrete wet bonding failure and RFRP–concrete wet bonding failure was mainly based on the large-scale concrete with peeled off concrete surface. RFRP effectively enhanced the wet adhesion performance of the interface with concrete in both normal and tangential directions. The interface bonding ability increased by 900% and 42%, respectively, compared with the control test pieces. The diameter of pelelith rock was found to be the most important factor affecting the shear wet bonding performance of the RFRP–concrete interface. The second important factor was the ratio of nano-kaolin. The optimum conditions for the best tangential anti-peeling ability of the RFRP–concrete structure were found to be the addition of 5-mm-diameter pelelith stone, 3% nano-kaolin, and glass cellosilk of 89 mm length. When the RFRP and the concrete were wet-bonded, the uncured cement mortar effectively filled the holes of the original pelelith rock and acted as a mechanical lock, thereby increasing the bonding stress.

Effective Method to Improve Anti-flaking Capacity of Cover Concrete to Textile

Investigation on Bonding and Overlapping Performance of Textile in Fine Grained Concrete

An Experimental Study on Improved Mechanical Behavior of Textile-Reinforced Concrete

Experimental Study on the Spalling Strength of Fiber Reactive Powder Concrete

Practical Method of Improving Bonding Behavior Between Fiber Textile and Mortar

Study on Bond Property Between High Performance Fine Concrete and Carbon Fibre Textile

Improved Mechanical Properties of Textile Reinforced Concrete Thin Plate

Experimental Research on Mechanical Performance of Hybrid Fiber Reinforced Cementitious Composites with Polyvinyl Alcohol Short Fiber and Carbon Textile

A Study on Thin Concrete Plate Reinforced with Textile

Bond Investigation Of Hybrid Textile With Self-Compacting Fine-Grain Concrete

Self-Compacting Concrete For Textile Reinforced Elements

Bond Properties and Experimental Methods of Textile Reinforced Concrete

Bond Performance of Hook-End Steel Fiber to the Mortars Cured for 360 Days

Study of Flexural Properties and Resistance Steadiness of Textile Reinforced Concrete

An Experimental Study on Bending Behavior of Cementitious Composites Reinforced in Combination with Carbon Textile and Short-Cut PVA Fiber

Effect of Polypropylene Fibers on Mechanical and Wetting Properties of Overall Superhydrophobic Foamed Concrete

Experimental research on the wet bonding properties between RFRP and concrete

High temperature mechanical performance and micro interfacial adhesive failure of textile reinforced concrete thin-plate

Effect of the addition of polypropylene fiber on concrete properties

The Calculational Analysis of Pullout Phenomena Textile Reinforced Concrete

Flexural behavior of warp knitted textile reinforced concrete impregnated with cementitious binder