The Influence of La addition on The Corrosion Resistance of AZ91 Magnesium Alloy

ZHOU Jing,FENG Zhiyong,ZHANG Jinling,WANG Shebin
DOI: https://doi.org/10.3969/j.issn.1007-9432.2013.05.005
2013-01-01
Abstract:The corrosion behavior of AZ91+0~0.65%(mass fraction)La magnesium alloy in 3.5% NaCl solution was studied by the static weightlessness experiments and potention dynamic polarization.The effects of La on the corrosion rate,corrosion potential and corrosion current of AZ91 magnesium alloy were characterized by scanning electronic microscopy(SEM),energy-dispersive spectroscopy(EDS),X-ray diffractometry(XRD) and the mechanism was explored.It was found that the corrosion rate decreased obviously as the La increased in AZ91 magnesium alloy in the static weightlessness experiments;the addition of La could improve the corrosion potential and decrease the corrosion current of AZ91 magnesium alloy in the electrochemical measurements.When the mass fraltion of La was 0.16%,the corrosion rate of AZ91 magnesium alloy decreased from 8 mg/(cm2·d)to 2 mg/(cm2·d),the corrosion current decreased from 0.527 mA to 0.014 mA,and the corrosion potential rised from-1.400 V to-1.328 V.The mechanism that La improved corrosion resistance of AZ91 magnesium alloy was that the addition of La refined the grain,transformed the morphology of β phase and improved the segregation of Al element.So the purity of the alloy and the electrode potential of substrate were improved and the corrosion resistance of AZ91 magnesium alloy was also improved.
What problem does this paper attempt to address?