Abstract:Statement of problem. Mechanical and thermal fatigue may affect ceramic restorations in the oral environment.Purpose. The purpose of this study was to determine the influence of thermal and mechanical cycling on the fracture load and fracture patterns of 3 machinable ceramics.Material and methods. Seventy-two human third molar teeth were prepared for bonding ceramic specimens of Sirona CEREC Blocs, IPS e.maxCAD, or inCoris ZI meso blocks. The 24 specimens of each ceramic were divided into 4 groups (n=6), which underwent no preloading (control), thermocycling (5 degrees C-55 degrees C, 2000 cycles), mechanical cycling (10(5) cycles, 100 N), and thermocycling (5 degrees C-55 degrees C, 2000 cycles) plus mechanical cycling (10(5) cycles, 100 N). The specimens were subsequently loaded to failure, and both stereomicroscopy and scanning electron microscopy were used to investigate the fracture patterns. The data were analyzed with 2-way ANOVA and the Fisher exact probability test (alpha=.05).Results. Mechanical and thermal cycling had a significant influence on the critical load to failure of the 3 ceramics. No significant difference was found between mechanical cycling for 105 times and thermocycling for 2000 times within the same ceramic. The specimens of inCoris ZI experienced significantly higher fracture loads for all the groups. The fracture patterns of the 3 machinable ceramics showed that failure mainly occurred at the cement-dentin interface.Conclusions. The effects of combined thermal and mechanical cycling on the fracture load of ceramics were more significant than any individual mode of cyclic fatigue. Overall, the inCoris ZI resisted thermal and mechanical fatigue better than the Sirona CEREC and IPS e.maxCAD.

BEHAVIOR OF CRACK PROPAGATION IN SOME BIO-CERAMICS

Fatigue Fracture Behavior of Zirconia Ceramic in Water Environment

Prediction of Fatigue Lifetime in Bio-Ceramics

The Predictions and Applications of Fatigue Lifetime in Alumina and Zirconia Ceramics

Mechanical and Environmental Factors in the Cyclic and Static Fatigue of A Machinable Glass-Ceramic

A Comparison of the Fracture Resistance of Three Machinable Ceramics after Thermal and Mechanical Fatigue.

Cracking of Porous Ceramics under Thermal Shock

Pores and cracking in ceramics

Interface Fatigue Crack Propagation in Ceramic Thermal Barrier Coatings

MODELING OF CRACK PROMGATION BEHMIOR IN WHISKER REINFORCED CERAMIC COMPOSITES

Fatigue Fracture Micro-Mechanism of a Machinable Glass-Ceramic

Effects of Residual Stresses on Strength and Crack Resistance in ZrO2 Ceramics with Alumina Coating

Thermal Shock and Ablation Behavior of Α-Cordierite Glass-Ceramic Coating on Porous BN/Si2N2O Ceramic

Research On The Cyclic Fatigue Behavior Of Zirconia Ceramics At The Room Temperature

In Vitro Cell Proliferation and Mechanical Behaviors Observed in Porous Zirconia Ceramics.

Strength Degradation and Lifetime Prediction of Dental Zirconia Ceramics under Cyclic Normal Loading.

Crack Arrest in Brittle Ceramics Subjected to Thermal Shock and Ablation

Effect of Pores on Crack Propagation Behavior for Porous Si3n4 Ceramics

The typical manners of dynamic crack propagation along the metal/ceramics interfaces: A molecular dynamics study

Effect of material parameters on thermal shock crack of ceramics calculated by phase‐field method

Molecular Dynamics Simulation of Crack Tip Processes in Ceria and Gadolinia Doped Ceria