Abstract:Emerging, flexible, textile-based supercapacitors have attracted considerable research interest in energy storage devices. However, very few flexible supercapacitors with good mechanical stability have been successfully developed based on traditional current collectors, especially for brittle transition metal oxides/hydroxides electrode material. This work reports a rational design of a nickel-deposited fiber fabric current collector, which displays excellent conductivity with sheet resistances of 0.355 Ω cm−2 before and 0.537 Ω cm−2 after 100,000 bending cycles. Further, a series of transition metal oxides/hydroxides were fabricated on the Ni-fabric current collector via an electrodeposition approach. The prepared Co(OH)2, NiO, and NiCo2O4 electrodes showed specific capacitances of 880.1, 589.1, and 725.7 F g−1 at 1 A g−1, respectively. In addition, when the electrodes with activated carbon (AC) were assembled into all-solid-state asymmetric supercapacitors, the as-prepared Co(OH)2//AC, NiO//AC, and NiCo2O4//AC devices delivered specific capacitances of 170.3, 265.6, and 219.8 mF ‍cm−2, respectively, with energy densities of 1.24, 1.63, and 1.35 mWh ‍cm−3 at 1 mA ‍cm−‍2. The capacitances of these devices retained high values of 92.8%, 94.4%, and 95.1% even after 1000 cycles of bending and folding by the automatic test machine. These results indicate that metal oxide compound electrodes based on a Ni-fabric current collector provide a universal strategy for high-performance and ultra-flexible supercapacitors.

NiCo Oxyfluoride Non-Woven Cloth with Ultra-High Area Capatitance for Wearable Supercapacitors

Nickel-Cobalt Sulfide Nonwoven Cloth with UltraHigh Areal Capacitance for Flexible Supercapacitors

Monocrystalline FeMnO3 on Carbon Cloth for Extremely High-Areal-Capacitance Supercapacitors

Ultrathin porous NiCo2O4 nanosheet arrays on flexible carbon fabric for high-performance supercapacitors.

Nickel cobaltite nanowire arrays grown on nitrogen-doped carbon nanotube fiber fabric for high-performance flexible supercapacitors

Facilely synthesized porous NiCo2O4 flowerlike nanostructure for high-rate supercapacitors

High-performance supercapacitor based on metal oxide coated fibrous electrode

Self-etching Ni–Co Hydroxides@ni–cu Nanowire Arrays with Enhancing Ultrahigh Areal Capacitance for Flexible Thin-Film Supercapacitors

Porous NiCo2O4–FeCo2O4 Nanowire Arrays As Advanced Electrodes for High-Performance Flexible Asymmetric Supercapacitors

Iron Oxides Nanobelt Arrays Rooted in Nanoporous Surface of Carbon Tube Textile As Stretchable and Robust Electrodes for Flexible Supercapacitors with Ultrahigh Areal Energy Density and Remarkable Cycling-Stability

A High-performance Flexible Pseudosupercapacitor Constructed on Conductive Cloth

Wearable High‐Performance Supercapacitors Based on Silver‐Sputtered Textiles with FeCo2S4–NiCo2S4 Composite Nanotube‐Built Multitripod Architectures As Advanced Flexible Electrodes

Hierarchically nanobranch structured freestanding metallic mesh electrode for high-performance transparent flexible supercapacitor

Growth of Nife2o4 Nanoparticles on Carbon Cloth for High Performance Flexible Supercapacitors

Carbon Cloth Coated with NiO Nanoparticles and Graphene for Flexible Asymmetric Supercapacitors

Constructing nickel cobaltate @nickel-manganese layered double hydroxide hybrid composite on carbon cloth for high-performance flexible supercapacitors

Strongly coupled carbon quantum dots/NiCo-LDHs nanosheets on carbon cloth as electrode for high performance flexible supercapacitors

Mno2@Nickel Nanocone Arrays With High Areal Capacitance For Flexible Zincion Supercapacitor

Facile Preparation of Carbon Nanotubes/Cellulose Nanofibrils/Manganese Dioxide Nanowires Electrode for Improved Solid-Sate Supercapacitor Performances

A universal strategy for ultra-flexible inorganic all-solid-state supercapacitors

Sulfide‐Based Nickel‐Plated Fabrics for Foldable Quasi‐Solid‐State Supercapacitors