Sulfide‐Based Nickel‐Plated Fabrics for Foldable Quasi‐Solid‐State Supercapacitors

Zhihao Wei,Tao Liu,Liuyang Zhang,Jiaguo Yu

DOI: https://doi.org/10.1002/eem2.12201

2021-06-08

Abstract:<p>Smart wearable market is burgeoning. And flexible energy storage is crucial to cope with its development. The commonly-used metal-based current collectors are heavy with limited flexibility. Other carbon-based current collectors are expensive and fragile. Moreover, the poor interface between active material and current collector leads to unsatisfactory stability. Herein, these two issues are attempted to be solved by using cheap and lightweight polyester-based fabrics as well as in-situ growth. A deposited thin layer of nickel on the fabrics not only enhances the conductivity, but also serves as the sacrificial precursor for the growth of active materials. Thus, intimate contact is secured via chemical bonding. The electrode with ternary (metal-inorganic-organic) components shows excellent electrochemical performance. Namely, high areal capacity is realized (2.2 C·cm^-2 at 2 mA·cm^-2), which is far superior to its rigid nickel-foam-based counterpart. Furthermore, an all-solid-state supercapacitor device was assembled. The device provides an areal capacity of 2.03 C·cm^-2 at the current density of 2 mA·cm^-2. It realizes an energy density of 0.45 mWh·cm^-2 when the power density is 1.6 mW·cm^-2. This work offers a feasible and cost-efficient way for fabricating electrode materials with excellent performance for portable supercapacitors.</p>

materials science, multidisciplinary

What problem does this paper attempt to address?

### Problems the paper attempts to solve

This paper aims to solve the following two main problems:

1. **Problems with current collectors in existing supercapacitors**:
- **Weight and flexibility problems**: Commonly used metal - based current collectors (such as nickel foam) are heavy and have limited flexibility, which are not suitable for portable electronic devices.
- **Poor interface contact problem**: The interface contact between the active material and the current collector is poor, resulting in unstable electrode performance.

2. **Improving the electrochemical performance of supercapacitors**:
- **Increasing areal capacity**: By using low - cost, lightweight polyester - based fabrics as current collectors and adopting in - situ growth techniques to enhance conductivity and chemical bonding of active materials, high areal capacity can be achieved.
- **Increasing energy density**: By optimizing electrode materials and structural design, the energy density of supercapacitors is increased, making them have more extensive application prospects in portable and flexible energy storage devices.

### Solutions

To overcome the above problems, the authors adopted the following methods:

1. **Using low - cost, lightweight polyester - based fabrics as current collectors**:
- A thin layer of nickel is deposited on the fabric surface, which not only enhances conductivity but also serves as a sacrificial precursor for the growth of active materials.
- Tight contact between the active material and the current collector is achieved through chemical bonding to ensure structural integrity.

2. **Adopting in - situ growth techniques**:
- Binary metal sulfides (such as CoNi₂S₄ and Ni₃S₂) are in - situ grown on nickel - coated fabrics by hydrothermal method to form ternary (metal - inorganic - organic) composites.
- This composite has multiple redox sites and diverse oxidation states, which significantly improves the electrochemical performance.

3. **Assembling all - solid - state supercapacitors**:
- All - solid - state supercapacitors are assembled using PVA/KOH gel as electrolyte.
- The test results show that the device exhibits good electrochemical performance and mechanical stability at different bending angles.

### Experimental results

The experimental results show that the prepared electrodes have the following significant advantages:

1. **High areal capacity**: At a current density of 2 mA·cm⁻², the areal capacity reaches 2.2 C·cm⁻², which is 30% higher than that of the electrodes using nickel foam substrates.
2. **Good cycling stability**: After 5000 cycles, the performance still remains above 80%.
3. **Good flexibility and mechanical properties**: Under multi - angle bending conditions (even 180°), the electrochemical performance hardly changes.
4. **Economical and simple synthesis method**: It shows high potential in industrial applications.

### Conclusions

In this paper, nickel - coated fabrics are successfully prepared and partially converted into CoNi₂S₄/Ni₂S₃@NPF electrodes with three - dimensional structures by hydrothermal method. This method eliminates the heavy - metal current collectors and harmful binders used in the traditional slurry coating method, ensures structural integrity, and solves the problem of active material falling off or being damaged during the electrochemical cycling process. Thanks to these characteristics, the areal capacity of this flexible and lightweight electrode reaches 2.2 C·cm⁻². In addition, both the aqueous and all - solid - state devices assembled with this electrode show good performance. In particular, in the all - solid - state device, the maximum energy density reaches 0.45 mWh·cm⁻² (power density is 1.5 mW·cm⁻²). This work provides an example for the successful development of flexible all - solid - state supercapacitor devices and is expected to inspire more research efforts in related fields.