Abstract:Strain-controlled fatigue tests were performed on a cast Mg–8Gd–3Y–0.5Zr (wt. %, GW83K) alloy to investigate the effect of microstructure on strain localization and fatigue crack initiation. The results show that, in T4 alloys, a large number of basal slips in individual grains and most grains in the bulk material are involved in plastic deformation and fatigue damage because persistent slip bands (PSBs) are dense and uniform. The interaction between dense PSBs and grain boundaries (GBs) occurs continuously along a wide range of GBs, resulting in uniform distribution of residual strains along GBs. The grain-level strain localizations within and among grains are effectively alleviated. In T6 alloys, however, due to the sparse and inhomogeneous PSBs, only a few basal slips in individual grains and only a few grains in the bulk material participate in plastic deformation and fatigue damage. The interaction sites between sparse PSBs and GBs is significantly limited, which leads to highly concentrated deformation at a few specific areas of the GBs. It results in high trans-granular strain localization in long range stretching across both grain interiors and GBs in short cycles. The strain localizations within and among grains are relatively aggravated. Moreover, the saturated strains of the T4 alloys are much larger than those of the T6 alloys. Therefore, under the same loading condition, it takes more cycles for T4 alloys, while fewer cycles for T6 alloys, to reach the saturation strains and initiate micro-cracks. In other words, the crack initiation life of T4 alloys is much longer than that of T6 alloys.

Effect of Microstructure on Small Fatigue Crack Initiation and Early Propagation Behavior in Mg-10Gd-3Y-0.3Zr Alloy

Small Crack Initiation and Early Propagation in an As-Extruded Mg-10Gd-3Y-0.5Zr Alloy in High Cycle Fatigue Regime

Small Crack Behavior of Extruded Mg-Gd-Y-Zr Alloy under High Cycle Fatigue

Cyclic Deformation And Correspondent Crack Initiation At Low-Stress Amplitudes In Mg-Gd-Y-Zr Alloy

The Effect of Microstructure on the Plastic Strain Localization and Fatigue Crack Initiation in Cast Mg–8Gd–3Y–0.5Zr Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Localized dislocation interactions within slip bands and crack initiation in Mg-10Gd-3Y-0.3Zr alloy

Effect of Microstructure Inhomogeneity and Crack Initiation Environment on the Very High Cycle Fatigue Behavior of a Magnesium Alloy

A Study of Fatigue Damage Development in Extruded Mg–Gd–Y Magnesium Alloy

Effect of Microstructure on Tensile and Fatigue Properties of Cast Mg–10Gd–2Y–0·5Zr Alloy

Low cycle fatigue of a rare-earth containing extruded magnesium alloy

In-Situ Study on the Tensile Deformation and Fracture Mechanism of a Bimodal-Structured Mg-Gd-Y Alloy

The Micro-Mechanism of Fatigue Crack Propagation for a Forged Mg–Zn–Y–Zr Alloy in the Gigacycle Fatigue Regime

Effect of chemical composition on the microstructure, tensile properties and fatigue behavior of sand-cast Mg–Gd–Y–Zr alloy

Effects of Microstructure on Fracture Toughness of Wrought Mg-8Gd-3Y-0.5Zr Alloy

Effect of long-period stacking ordered structure on very high cycle fatigue properties of Mg-Gd-Y-Zn-Zr alloys

Effect of Bimodal Microstructure on the Tensile Properties and Fracture Toughness of Extruded Mg-9Gd-4Y-0.5Zr Alloy

Plastic Strain Accommodation and Crack Initiation in a Randomly-Oriented Mg-8y-1zr Magnesium Alloy During Accumulated Tensile Deformation

Effects of Nanoprecipitates and LPSO Structure on Deformation and Fracture Behaviour of High-Strength Mg-Gd-Y-Zn-Mn Alloys

Quantitative assessment of the microstructural factors controlling the fatigue crack initiation mechanisms in AZ31 Mg alloy

Effect of Frequency on High-Cycle Fatigue Properties and Microstructure Evolution of Mg-9Gd-3Y-1Zn-0.8Zr Extruded Rare Earth Magnesium Alloy