Microstructures and Mechanical Properties of Laser-Arc Hybrid Welded Dissimilar Pure Copper to Stainless Steel

Yunfei Meng,Xinwei Li,Ming Gao,Xiaoyan Zeng
DOI: https://doi.org/10.1016/j.optlastec.2018.09.050
IF: 4.939
2018-01-01
Optics & Laser Technology
Abstract:Laser-cold metal transfer hybrid welding was applied to the butt-welding of T2 copper/304 stainless steel (Cu/304SS) dissimilar joint by deviating the laser beam from the edge of the weld seam to the Cu plate. Under the optimal laser offset (Delta D = 0.5-1.0 mm), an acceptable weld with uniform surface morphology and free of visible defect was obtained. All the joints obtained at the optimal Delta D fractured at the Cu side, with the maximum tensile strength reached up to 215 MPa, approximately to that of T2 copper (200-240 MPa). The variations of the weld mechanical properties were well corresponding to the observed microstructure changes. Too small Delta D ( < 0.5 mm) resulted in the excess melting of 304SS and formation of the macrosegregations of the Fe-rich peninsula and islands in the fusion zone, which deteriorated the weld mechanical properties. While increasing the Delta D decreased the amount of the melted 304SS, and benefited to from the Cu-rich matrix and inner uniformly distributed Fe-rich particles, which strengthened the weld. However, excess Delta D ( > 1.0 mm) weakened the weld because only coarse Cu columnar grains formed.
What problem does this paper attempt to address?