Promotion effect of cerium in ZSM-22 zeolite on the hydroisomerization of n-hexadecane
Qiang Wang,Ley Boon Sim,Jianrong Xie,Songshou Ye,Jile Fu,Jiexiang Wang,Nuowei Zhang,Jinbao Zheng,Binghui Chen
DOI: https://doi.org/10.1016/j.micromeso.2023.112720
IF: 5.876
2023-07-13
Microporous and Mesoporous Materials
Abstract:The study fabricated ZSM-22 zeolites with Ce/Al molar ratios ranging from 0 to 1, which were subsequently loaded with Pt to perform n-hexadecane hydroisomerization. Various methods, such as XRD, 29 Si NMR, FTIR, UV–Vis, XPS, and H 2 -TPR, confirmed the direct evidence of Ce incorporation into the zeolite framework, and the framework Ce content was of a volcanic nature. Furthermore, the study observed successful manipulation of textural and acidity properties of the samples through variation of the Ce content, as shown by N 2 -physisorption, NH 3 -TPD, and Py-IR. Increasing Ce content led to retardation of micropore diffusion due to lower micropore volume and surface area, as well as an increase in the distribution of weak Brønsted acid sites, which suppressed outside-of-pore cracking reactions. These changes rendered improved i-hexadecane selectivity and catalyst stability for Pt/ZSM-22. At a Ce/Al molar ratio of 0.5 with a WHSV of 12 h −1 , the high selectivity to monobranched isomers resulted in a yield exceeding 75 wt%.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology, applied