Abstract:Using the Raney Fe-Al alloy as the precursor for Fe and Al, and tetrapropylammonium hydroxide (TPAOH) as both the base for the leaching of the alloy and the template for the synthesis of HZSM-5, we synthesized the skeletal Fe core-HZSM-5 shell catalysts (Raney Fe@HZSM-5) via a facile one-pot hydrothermal strategy. The thickness of the zeolite shell was adjusted by varying the hydrothermal time. The catalysts were characterized by inductively coupled plasma-atomic emission spectroscopy (ICP-AES), N-2 physisorption, X-ray powder diffraction (XRD), temperature-programmed desorption of NH3 (NH3-TPD), and scanning electron microscopy (SEM). It was identified that the Raney Fe-Al alloy was more suitable than the rapidly quenched Fe-Al alloy as the precursor to the skeletal Fe core, since the skeletal Fe catalyst alkali-leached from the former produced more long-chain hydrocarbons during the Fischer-Tropsch synthesis (FTS) reaction for successive cracking and isomerization. A complete HZSM-5 shell was obtained only after above 24 h of hydrothermal treatment. With the hydrothermal time from 2 d to 8 d, the thickness of the compact HZSM-5 shell increased from 1.3 mu m to 9.7 mu m, the relative crystallinity increased steadily, while the SiO2/Al2O3 ratio remained essentially constant, and the amount of the acid sites is parallel to the thickness of the zeolite shell. In the FTS reaction using syngas with the H-2/CO molar ratio of 2 and at 543 and 2.0 MPa, the CO conversion and the selectivity to the gasoline fraction (C-5 similar to C-11 hydrocarbons) evolved in a volcanic trend with the shell thickness, suggesting the existence of an optimal amount of the acid sites, while less or more is adverse to the activity and selectivity to the gasoline fraction. The Raney Fe@HZSM-5 catalyst hydrothermally treated for 4 d exhibited the highest CO conversion of 92% and the selectivity to the gasoline fraction of 71%, along with an iso-paraffin to n-paraffin ratio of 1.9. At the n(H-2)/n(CO) ratio of 1, the selectivity to the gasoline fraction and the iso-paraffin to n-paraffin ratio were further improved to 73% and 2.1, respectively, which shows promise for this catalyst to transform the coal- or biomass-derived syngas to high-octane number gasoline.

Synthesis of hierarchical Fe-incorporated ZSM-5 molecular sieves with an Fe-based metal-organic framework as a mesoporogen and iron source for catalytic pyrolysis of alkanes

Synthesis and Physicochemical Characterization of Hierarchical ZSM-5: Effect of Organosilanes on the Catalyst Properties and Performance in the Catalytic Fast Pyrolysis of Biomass

Preparation of Fe@Si/S-34 Catalysts and Its Catalytic Performance for Syngas to Olefins

One-pot green synthesis of Fe-ZSM-5 zeolite containing framework heteroatoms via dry gel conversion for enhanced propylene selectivity of catalytic cracking catalyst

HZSM-5 supported with N-doped Fe for microwave catalytic pyrolysis of lignin

The conversion of biomass to light olefins on Fe-modified ZSM-5 catalyst: Effect of pyrolysis parameters

Facile synthesis of hierarchical macro/microporous ZSM-5 zeolite with high catalytic stability in methanol to olefins

Catalytic pyrolysis performance of alkanes to light olefins over bifunctional ZSM-5 zeolites

Facile Synthesis of Nanosheet-Stacked Hierarchical ZSM-5 Zeolite for Efficient Catalytic Cracking of n-Octane to Produce Light Olefins

Catalytic Pyrolysis of Biomass Over Fe-Modified Hierarchical ZSM-5: Insights into Mono-Aromatics Selectivity and Pyrolysis Behavior Using PY-GC/MS and TG-FTIR

Enhanced Fischer-Tropsch synthesis performance on fe + ZSM5 bifunctional catalysts

Tuning Hierarchical ZSM-5 Zeolite for Both Gas- and Liquid-Phase Biorefining

Reaction characteristics of maximizing light olefins and decreasing methane in C5 hydrocarbons catalytic pyrolysis

Isomorphously Substituted [Fe,Al]ZSM-5 Catalysts for Methane Dehydroaromatization

Fabrication and Catalytic Performance of Mn Loaded Hierarchical Fe-Zsm-5 Zeolite for Chlorobenzene Combustion

Design of novel porous Fe2O3 cage catalyst for production of gasoline fuels via coupling Fischer-Tropsch with zeolite cracking

Effect of Shell Thickness on Skeletal Fe@HZSM-5 Core-Shell Catalysts for Fischer-Tropsch Synthesis

Hierarchical ZSM-5 Supported CoMn Catalyst for the Production of Middle Distillate from Syngas

Simultaneous Enhancement of Aromatic Products and Catalytic Lifetime for Catalytic Re-forming of Lignite Pyrolysis Volatiles over a Self-Assembled Hierarchical Core–Shell ZSM-5@Silicalite-1 Zeolite

Direct Conversion of Syngas to Gasoline Ranged Olefins over Na Impellent Fe@NaZSM-5 Catalyst

Advanced Synthesis of Hierarchically Porous Zeolite Catalysts Utilizing Biomass Templates for the Catalytic Pyrolysis of Stearic Acid into Short-Chain Olefins