Abstract:The present work investigated the effects of magnetic field annealing on the magnetic properties, mechanical properties and microstructure of the Fe80Si9B11 amorphous alloys. The results show that the soft magnetic properties (SMPs) were obviously improved after the samples were annealed below the crystallization temperature with a 1 T magnetic field. The atom probe tomography (APT) results showed that the magnetic field has little effect on the element distribution of the annealed samples at 653 K. The results of XRD and TEM showed that the 653 K x 0 T sample included a few nanocrystals and an amorphous matrix while the 653 K x 1 T sample still retained an amorphous structure. It is worth noting that a large number of spherical symmetry clusters and a small number of translational symmetry clusters can be observed in the 653 K x 1 T sample. Many translational symmetry clusters, and a few spherical symmetry clusters, can be identified in the 693 K x 1 T sample. Both good soft magnetic properties (SMPs) and acceptable mechanical properties were obtained after the sample was annealed at 653 K. Compared with that of the as-cast sample, the values of maximum magnetic flux intensity (B-m), elastic modulus (E-r) and hardness increased by 13.7%, 36.6% and 9.4%, respectively, while the values of coercivity (H-c) and hysteresis loss (P-u) decreased by 71.5% and 68.2%, respectively. After the sample was annealed at 693 K, the SMPs exhibited a deterioration, and Er and hardness also dropped sharply. Based on the above results, the mechanism of the microstructural change for Fe80Si9B11 amorphous alloys related to the magnetic field annealing conditions was proposed. The relationship between the soft magnetic properties, mechanical properties, and the microstructure of the sample was also discussed. This paper provides a basis for the further improvement the SMPs of the Fe80Si9B11 amorphous ribbons by controlling the microstructure.

Improvement of Soft Magnetic Properties for Distinctly High Fe Content Amorphous Alloys Via Longitudinal Magnetic Field Annealing

Excellent Magnetic Softness-Magnetization Synergy and Suppressed Defect Activation in Soft Magnetic Amorphous Alloys by Magnetic Field Annealing

The Effects of Magnetic Field Annealing on the Magnetic Properties and Microstructure of Fe 80 Si 9 B 11 Amorphous Alloys

Influence of Annealing Temperature on Microstructure and Magnetic Properties of FeSiNbCuBP Amorphous Alloys

The Effect of Annealing on the Soft Magnetic Properties and Microstructure of Fe82Si2B13P1C3 Amorphous Iron Cores

Influence of Annealing Process on Soft Magnetic Properties of Fe-B-C-Si-P Amorphous Alloys

Improvement of soft-magnetic properties for Fe-based amorphous alloys with high saturation polarization by stress annealing

Effect of longitudinal magnetic field annealing process on the properties and structures of soft magnetic Fe73.7Si15.3Cu1Nb3B7 nanocrystalline alloys

Magnetic Softening of the Fe83Si3B11P2Cu1 Amorphous/nanocrystalline Alloys with Large-Size Pre-Existing Α-Fe Grains by High Heating-Rate Annealing

Effect of Fe Content on the Soft Magnetic Properties of Fe-Rich FeSiBC Amorphous Alloy

Significant improvement of soft magnetic properties for FeCoSiBC amorphous alloy cores by magnetic field annealing

Effect of Longitudinal Magnetic Heat Treatment on Soft Magnetic Properties of Fe-based Amorphous-Nanocrystalline with High Saturation Magnetic Induction

Improving the Amorphous Forming Ability and Magnetic Properties of FeSiBPCu Amorphous and Nanocrystalline Alloys by Utilizing Carbon

Structural Origin of Magnetic Softening in a Fe-based Amorphous Alloy Upon Annealing

Effect of annealing process on soft magnetic properties of Fe91.63B1.27Si7.09 amorphous strip

Synthesis of Novel FeSiBPCCu Alloys with High Amorphous Forming Ability and Good Soft Magnetic Properties

Effect of Magnetic Field Annealing on Soft Magnetic Properties of Co71Fe2Si14-xB9+xMn4 Amorphous Alloys with Low Permeability

Modulating Magnetic Properties of High Entropy Soft FeSiB(P)Cu Alloys with Excellent GFA Via Α-Fe(si) Grain Preferential Growth Mechanism

Effect of Annealing on the Magnetic Properties of FeCoNiCuNbSiB Soft Magnetic Alloys

Structure and soft magnetic properties of Fe-Si-B-P-Cu nanocrystalline alloys with minor Mn addition

Ultra-fine microstructure and exceptional low coercivity developed in a high-Bs Fe-Si-B-P alloy by co-alloying Ni, Mo, and Cu