Temperature Dependence of the Transverse Piezoelectric Properties in the [001]-Poled 0.25Pb(in1/2nb1/2)o3-0.42Pb(mg1/3nb2/3)o3-0.33pbtio3 Single Crystal with Alternating Current Treatment
Ming Ma,Song Xia,Kexin Song,Haisheng Guo,Zhuo Xu,Zhenrong Li
DOI: https://doi.org/10.1063/5.0044618
IF: 2.877
2021-01-01
Journal of Applied Physics
Abstract:In this work, the transverse piezoelectric properties of the pre-direct current poled (DCP) 0.25Pb(In1/2Nb1/2)O3-0.42Pb(Mg1/3Nb2/3)O3-0.33PbTiO3 (0.25PIN-0.42PMN-0.33PT) single crystals were enhanced by the alternating current treatment (ACT) of 10 kVp/cm (5.8 kVrms/cm), 50 Hz, and 20 cycles. The transverse piezoelectric constant d31 of −1560 pC/N and electromechanical coupling coefficient k31 of 0.92 at room temperature were achieved in the DCP-ACT crystal, which were, respectively, 80% and 11% higher than those of the DCP crystal (d31=−870pC/N,k31=0.83) . Meanwhile, the elastic compliance constant S11E and dielectric permittivity ε33T/ε0 of the DCP-ACT crystal were, respectively, 78% and 46% higher than those of the DCP crystal. Based on the temperature dependence of dielectric properties and resonance curves, the d31, ε33T/ε0, and S11E of the DCP-ACT crystal were higher than those of the DCP crystal in the R phase region. The DCP-ACT crystal also showed a higher TFerro (110 °C) than the DCP crystal (96 °C), which was related to the intermediate phase induced by ACT. The d31 at Tferro of the DCP-ACT crystal can be −3810 pC/N, which was 2.3 times that of the DCP crystal (−1680 pC/N). In the T phase region, the DCP-ACT crystal presented a high ε33T/ε0 and attenuated impedance resonance. Moreover, ACT also affected the ferroelectric to paraelectric phase transition. This could be related to the nanoscale heterogeneous polar region induced by ACT, which enhanced the inhomogeneous state in the relaxor-based ferroelectric single crystal. ACT is a potential way for improving the transverse piezoelectric properties of the PIN-PMN-PT single crystal.