Corrosion Behavior of Fluorine-Doped Calcium Phosphorus Coating on AZ31 Alloy with Various Chemical Conversion Parameters
Liuwei Zheng,Lifei Wang,Hua Chai,Chaoyang Yang,Qiuyan Huang,Zhipeng Ge,Hongxia Wang,Weili Cheng,Hua Zhang,Fugang Qi,Xiaoye Zhou,Hanuma Reddy Tiyyagura,Kwang Seon Shin
DOI: https://doi.org/10.1007/s11665-024-09671-5
IF: 2.3
2024-06-05
Journal of Materials Engineering and Performance
Abstract:To improve the corrosion resistance of biomedical magnesium alloys, fluoride ions (0.3 M, 0.5 M, and 0.7 M) were added to a solution of water containing 0.042 mol/L Ca(NO 3 ) 2 ·4H 2 O and 0.025 mol/L NH 4 H 2 PO 4 . Calcium Phosphorus (Ca-Ph) coatings with different morphology and corrosion resistance were obtained by changing the temperature and fluorine ion content to explore the growth mechanism of fluorine-doped Calcium Phosphorus (F-CaP) coating. The surface morphologies, and chemical compositions of these coatings were characterized by x-ray diffraction, scanning electron microscopy and energy-dispersive spectroscopy, and the corrosion resistances of the coatings were investigated by electrochemical tests and immersion tests. The results show that temperature has a great effect on the morphology of F-CaP coating. An increase in the temperature accelerated the reaction rate of the ions during the deposition process, and the low amount of fluoride prevented the F-CaP coating from fully covering the surface of the matrix. When the amount of doped fluorine was 0.5 M at 60 °C, the complete and compact coating morphology effectively protected the AZ31 magnesium alloy from the corrosion of simulated body fluids.
materials science, multidisciplinary