Abstract:Titania-based nanocomposites have recently attracted much attention due to their unique structure and properties. Titania has been known to have three crystal phases: brookite, anatase and rutile. The anatase titania has the highest photoactivity than the other two phases. Meanwhile Ohtani et al. [1] reported that amorphous titania has a negligible photoactivity compared to the crystalline titania. Much work has been conducted on the optimization of catalytic properties of titania used in the photodegradation of organic pollutants in water by either using modified titania or thin titania films. Many researches indicated that dopants, such as many oxides, can effectively suppress the transformation of anatase into rutile by improving the onset transformation temperature [2]. Silica-titania mixed oxide is considered a potential candidate because it is used as not only a good photocatalyst itself but also a support material for other chemical reaction catalysts [3, 4]. 30SiO2/TiO2 powders (30 denotes the weight percent of silica) were prepared by sol-gel process. Ti(OBu n )4 and TEOS were used as precursors of titania and silica respectively. After TEOS was stirred in a mixture solution of pure ethanol, distilled water and hydrochloric acid for 1 h, Ti(OBu n )4 was added slowly into the mixture. The sol of SiO2/TiO2 was obtained after another two hours’ vigorous stirring and cooled to room temperature. The gel was calcined at different temperatures and then ground into fine powders. The distilled water solution of methyl orange (with a concentration of 25 mg/L) was chosen for photodegradation. 0.2 g powders were added into 40 ml of the above solution with vigorous agitation under the mercury light. A 756MC UV-VIS spectrometer was used to record the change of concentration of the methyl orange. FT-IR spectra was obtained by a Bruker EQUINOX55 spectrometer. TEM and HREM observations were carried out using a Jeol-2010 electron microscope. The XRD patterns were made in a D/max3A diffractometer with Cu Kα radiation. The crystallite size of powders was determined by Scherrer equation. Electron spin resonance measurements were made with a Bruker paramagnetic spectrometer. X-ray photoelectron spectroscopy (XPS) spectra of the sample were obtained with an NP-1 using the Mg Kα excitation source and the binding energies referenced to the C1s hydrocarbon line at 284.6 eV. The atomic ratios were obtained by intergrating the areas under the peak. Photodegradation for methyl orange with 30SiO2/ TiO2 samples calcinated at different temperature under UV irradiation is illustrated in Fig. 1. The results of other samples heated at temperatures higher than 850 ◦ C were not shown in this figure because further increase of the calcination temperature decreased the decomposition rate. It can be seen that decomposition rate of the samples fired at 400 ◦ C and 500 ◦ Ci s low. When the calcination temperature was further increased to 600 ◦ C, the higher photoactivity than Degussa P25’s was obtained. The sample heated at 800 ◦ C has the best photoactivity about 2 times higher than the Degussa P25.

Photoluminescence and Photodegradation Properties of SiO2@TiO2:Sm3+ with Different Coating Effects

SiO2@TiO2:Sm3+ with Diverse Phase Structure and Morphology: Photoluminescence and Simulated Solar Light-Activated Photodegradation Properties

Photoluminescence Properties and Photocatalytic Activities of SiO2@TiO2:Sm3+ Nanomaterials

Multisite Luminescence and Photocatalytic Properties of TiO2:Sm3+ and TiO2:Sm3+@TiO2/TiO2:Sm3+@SiO2 Luminescent Enhancement Materials

Photocatalytic Degradation of Methyl Orange in Water by Samarium-Doped TiO<sub>2</sub>

Photocatalytic and Photoluminescence Properties of Core-Shell SiO2@TiO2:Eu3+,Sm3+ and Its Etching Products

Luminescence properties of Ti3+ doped methyltriethoxysilane modified SiO2 composite coating

Degradation of Methylene Blue Solution of TiO2 Doped with Sm3+ Loaded Porous Ceramics

SiO2@TiO2:Eu3+ and Its Derivatives: Design, Synthesis, and Properties

Photodegradation of Methyl Orange by V5+ and Ho3+ Co-doped TiO2

Photoinduced hydroxyl radical and photocatalytic activity of samarium-doped TiO2 nanocrystalline

Sol–gel auto-combustion synthesis of samarium-doped TiO2 nanoparticles and their photocatalytic activity under visible light irradiation

Fabrication of hydroxyl group modified monodispersed hybrid silica particles and the h-SiO2/TiO2 core/shell microspheres as high performance photocatalyst for dye degradation

Enhanced photoactivity of silica-titania binary oxides prepared by sol-gel method

Influence of Ho3+/La3+-doping on photocatalytic activity of TiO2 for methyl orange degradation

Photoluminescence and photocatalytic activity of flowerlike hierarchical TiO2:Sm3+ microspheres

Effects of Samarium Dopant on Photocatalytic Activity of TiO2 Nanocrystallite for Methylene Blue Degradation

Salicylic Acid-Modified Sm-TiO 2 for Photoluminescence and Photocatalysis under Real Sunlight: Synergistic Effects between Ligand-to-Metal Charge Transfer (LMCT) and Sm 3+ Dopant

Competitive Sensitization Effect Towards Luminescence-tuned Lanthanide-doped TiO2/SiO2 Core-shell Nanoparticles for Enhanced Responsivity Oxygen Detection

Photoluminescence properties of samarium-doped TiO2 semiconductor nanocrystalline powders

Preparation of silicon-doped TiO2 fiber and supported TiO2 and comparison study of their photocatalytic activity