Microstructure and Mechanical Properties of Cold Metal Transfer Welding-Brazing of Titanium Alloy (TC4) to Stainless Steel (304L) Using V-shaped Groove Joints

Gang Mou,Xueming Hua,Dongsheng Wu,Ye Huang,Wenhu Lin,Peizhi Xu

DOI: https://doi.org/10.1016/j.jmatprotec.2018.09.019

IF: 6.3

2019-01-01

Journal of Materials Processing Technology

Abstract:Wire feed speeds of 3.5, 4.5, and 5.5 m/min and offset positions of 1 and 2 were employed for this study with an ERCuSi-A weld wire. The microstructures of the joints, which include a Cu/Ti interface layer consisting of Ti2Cu, TiCu, and AlCu2Ti, a Cu-matrix seam consisting of Cu and petal-shaped Fe-Si-Ti intermetallics, and a Cu/Fe interface layer consisting of alpha-Fe and Cu, were studied. The formation enthalpy calculated from the Miedema model can explained the microstructure evolution mechanism. The interface thickness and ultimate tensile strength were found to increase with wire feed speed. The highest tensile strength of the joint was 294 MPa, fracturing at the Cu/Ti interface. Offsetting the welding torch to the TC4 side increased the amount and size of the Fe-Si-Ti intermetallics, degrading the tensile strength. Four fracture modes were proposed to differentiate the crack propagations in the joints, which were determined by the interfacial bonding strength and the Fe-Si-Ti intermetallics in the weld seam.