Abstract:In this study, a natural zeolite supported Co-B catalyst (Co-B/Zeolite) with a Co content of 10 wt.% was prepared by impregnation and chemical reduction method to release hydrogen gas from an alkaline sodium borohydride (NaBH 4 ) solution. The synthesized catalyst was characterized with various characterization techniques, including X-ray diffraction (XRD), X-ray fluorescence (XRF), inductively coupled plasma mass spectroscopy (ICP-MS), Brunauer–Emmett–Teller (BET), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), Fourier transform infrared (FTIR), and X-ray photoelectron spectroscopy (XPS), etc. It was found that the BET specific surface area of Co-B/Zeolite (26.03 m 2 g −1 ) was roughly double that of the zeolite (13.12 m 2 g −1 ). The Co ratio in the catalyst was found to be 12.02 wt.% by EDX analysis. ICP-MS examination of the catalyst revealed a B/Co atomic ratio of 0.64. No peaks associated with Co-B were observed in the XRD pattern of the catalyst, indicating the amorphous nature of the component. Parameters that have significant effects on the hydrolysis reaction, such as catalyst amount, sodium hydroxide and sodium borohydride concentrations, and reaction temperature, were investigated. The hydrogen generation rate (HGR) was found to be 1732 mL min −1 g cat −1 in the presence of 100 mg of Co-B/Zeolite in 5 wt.% NaOH and 5 wt.% NaBH 4 solution at 50 °C. The experimental results were well fitted to the zero-order kinetic model ( k 0 = 0.0296–0.1619 mol min −1 g cat −1 for 20–50 °C). The activation energy ( E a ) of the catalytic reaction was found to be 44.98 kJ mol −1 . Meanwhile, the reusability evaluations showed that the catalyst preserves high stability and can still sustain 73% of its initial activity after 5 catalytic cycles.

Porous Co3O4 Nanoplatelets As Efficient Catalyst Precursor for Hydrogen Generation from the Hydrolysis of Alkaline Sodium Borohydride Solution

Efficient Hydrogen Generation From The Nabh4 Hydrolysis By Cobalt-Based Catalysts: Positive Roles Of Sulfur-Containing Salts

A highly active Co-B catalyst for hydrogen generation from sodium borohydride hydrolysis

Development of Al2O3-supported nanobimetallic Co-La-B catalyst for boosting hydrogen release via sodium borohydride hydrolysis

Nickel- and Cobalt-Based Catalysts for Hydrogen Generation by Hydrolysis of Borohydride

Bimetallic Pt-Ni Nanoparticles Confined in Porous Titanium Oxide Cage for Hydrogen Generation from NaBH4 Hydrolysis

Catalytic Hydrogen Evolution of NaBH4 Hydrolysis by Cobalt Nanoparticles Supported on Bagasse-Derived Porous Carbon

Magnetically Recovered Co and Co@Pt Catalysts Prepared by Galvanic Replacement on Aluminum Powder for Hydrolysis of Sodium Borohydride

Cobalt-based coordination polymer-derived hexagonal porous cobalt oxide nanoplate as an enhanced catalyst for hydrogen generation from hydrolysis of borohydride

Ultrafine cobalt nanoparticles supported on carbon nanospheres for hydrolysis of sodium borohydride

Preparation of Co–P–B/foam Ni catalyst and its catalytic performance for hydrogen production by hydrolysis of NaBH4 solution

Preparation of Co3−xCaxO4 nanostructure catalyst for improved hydrogen production from sodium borohydride

Kinetically promoted hydrogen generation by Ru nanoparticles decorated CoB2O4 on mesoporous carbon spheres with rich oxygen vacancies for NaBH4 hydrolysis

Graphene-Modified Co-B-P Catalysts for Hydrogen Generation from Sodium Borohydride Hydrolysis

Highly Stable and Controllable Cob/Ni-Foam Catalysts for Hydrogen Generation from Alkaline Nabh4 Solution

Carbon nanospheres supported bimetallic Pt-Co as an efficient catalyst for NaBH4 hydrolysis

Multifunctional Co-B-O@Co<sub>x</sub>B catalysts for efficient hydrogen generation

High-Surface-Area Co-Cu-B Monolithic Self-Supported Catalyst for Efficient Sodium Borohydride Hydrolysis

Simple synthesis of Cu2O–CoO nanoplates with enhanced catalytic activity for hydrogen production from ammonia borane hydrolysis

Efficient and Stable Co-B Catalyst Supported on Natural Zeolite for Hydrogen Generation from Hydrolysis of Alkaline NaBH4 Solution

In Situ Transformation of 3D Co3O4 Nanoparticles to 2D Nanosheets with Rich Surface Oxygen Vacancies to Boost Hydrogen Generation from NaBH4