The Effect of Er and Zr Ratio on Microstructure Evolution and Mechanical Properties of 6061 Aluminum Alloy
Xingkai Hou,Bolong Li,Jiaming Yin,Shasha Dong,Peng Qi,Zuoren Nie
DOI: https://doi.org/10.1088/1742-6596/2044/1/012103
2021-01-01
Journal of Physics Conference Series
Abstract:In the present study, the 6061 alloy was chosen as base alloy, and micro-alloying effect of different ratios of Er and Zr (2:1, 1:1) on microstructure evolution and mechanical properties was examined after T6 heat treatment. Hot rolling deformation was carried out at 450°C, then a solution aging heat treatment process was adopted at 570°C/0.5h+180°C/5h. The precipitation, recrystallization behaviors were characterized using transmission electron microscopy(TEM), scanning electron microscope(SEM) and electron backscattered diffraction(EBSD) techniques, the mechanical properties were tested using tensile tests. The results shown that recrystallization behavior was inhibited by co-additions of Er and Zr. With the increase of Er and Zr content, the recrystallized grain size and coarse Fe-rich phases at the grain boundaries decreased, the recrystallized grain distributed uniformly, the number of needle-like Mg2Si and granular Al3(Er, Zr) phases gradually increased. In 6061 alloy with Er/Zr ratio of 1, the distribution of precipitates were finer and more uniform, The uniformly distributed Al3(Er, Zr) phases pinned the grain boundaries, which effectively hindered the movement of grain boundaries. The tensile tests exhibited that the properties of 6061 alloy with Er/Zr ratio of 1 reached the highest level, i.e., tensile strength of 344.0MPa, the yield strength of 296.0MPa, and elongation of 17%.