Abstract:Tungsten oxide (WO3) is a strong candidate as the photoanode in photoelectrochemical (PEC) water splitting owing to its moderate band gap (2.6–3.2 eV) for wide light absorption and stable physicochemical properties. This work reports a morphology engineering strategy to fabricate voltage-induced terrace-like tungsten oxide (TW) film and its high-voltage performance as a photoanode for PEC water splitting. By controlling the anodization voltage, the morphology of the anodic WO3 film was altered, and their photoelectrochemical performances were compared. Anodization of the tungsten film in fluoride-containing H3PO4 leads to the growth of either irregular porous tungsten oxide layers or terrace-like tungsten oxide layers, depending on the anodic potentials. The possible growth mechanism of the porous oxide layer during anodization is proposed with a combination of the field-assisted dissolution model and the oxygen-bubble mold model. Under light irradiation, the photocurrent density was 3.0 mA cm–2 at 1.23 V vs RHE (VRHE) for annealed terrace-like WO3, which was almost 3 times larger than that of annealed porous WO3. As a photoanode, terrace-like WO3 films could generate hydrogen at 58 μmol cm–2 h–1 under simulated solar light, while porous WO3 films produced hydrogen with a slower rate of 28 μmol cm–2 h–1. The terrace-like WO3 films experience higher photoelectrochemical performance and incident photon-to-electron conversion efficiency (IPCE) than porous WO3 due to more regular nanostructure, smaller band gap, fast charge-transfer rate, and alleviated recombination rate. This study shows that morphology control can effectively enhance the photocurrent density and IPCE of photoanodes and suggests a practical direction for finding the optimal WO3 films for PEC water splitting.

CuWO4 Films Grown Via Seeding-Hydrothermal Method for Photoelectrochemical Water Oxidation

Self‐Assembled Urchin‐Like CuWO 4 /WO 3 Heterojunction Nanoarrays as Photoanodes for Photoelectrochemical Water Splitting

Nanoporous WO3 Films Synthesized by Tuning Anodization Conditions for Photoelectrochemical Water Oxidation

Fast annealing fabrication of porous CuWO 4 photoanode for charge transport in photoelectrochemical water oxidation

Elucidating the electronic structure of CuWO4 thin films for enhanced photoelectrochemical water splitting

Oriented CuWO 4 Films for Improved Photoelectrochemical Water Splitting

Oriented CuWO4 Films for Improved Photoelectrochemical Water Splitting

In situ formation of CuWO 4 /WO 3 heterojunction plates array films with enhanced photoelectrochemical properties

Facile Fabrication of Sandwich Structured WO3 Nanoplate Arrays for Efficient Photoelectrochemical Water Splitting.

Copper(Ii) Tungstate Nanoflake Array Films: Sacrificial Template Synthesis, Hydrogen Treatment, and Their Application As Photoanodes in Solar Water Splitting

Facile Synthesis of Tungsten Oxide Nanostructures for Efficient Photoelectrochemical Water Oxidation

Efficient Solar Water Oxidation by WO3 Plate Arrays Film Decorated with CoOx Electrocatalyst

High-Voltage Etching-Induced Terrace-like WO 3 Photoanode for Efficient Photoelectrochemical Water Splitting

Gradient surficial forward Ni and interior reversed Mo-doped CuWO4 films for enhanced photoelectrochemical water splitting

Platelike Wo3 from Hydrothermal Rf Sputtered Tungsten Thin Films for Photoelectrochemical Water Oxidation

Epitaxial Growth of Heteropolyacid-WO3 Vertical Heterostructures with Photo-Induced Charge Modulation for Enhanced Water Oxidation

Enhancement of the photoelectrochemical performance of CuWO 4 films for water splitting by hydrogen treatment

One-Step Rapid and Scalable Flame Synthesis of Efficient WO3 Photoanodes for Water Splitting.

Molybdenum Doped CuWO4 Nanoflake Array Films As an Efficient Photoanode for Solar Water Splitting

Hydrothermal Synthesis of the CuWO4/ZnO Composites with Enhanced Photocatalytic Performance

Photoelectrochemical water oxidation at FTO|WO3@CuWO4 and FTO|WO3@CuWO4|BiVO4 heterojunction systems: An IMPS analysis