Abstract:TC4 titanium alloy wire arc additive manufacturing (WAAM) is easy to produce coarse columnar β grain structure which affects mechanical properties. So in this paper, an innovative process of interpass milling assisted TC4 titanium alloy gas tungsten arc welding (GTAW) WAAM is proposed. The controlling interpass milling depth is used to improve the microstructure and mechanical properties of TC4 titanium alloy parts during the GTAW-WAAM. The results showed that the coarse columnar β grains and fine α phase were observed in the non-interpass milling part. When the interpass milling assistance GTAW-WAAM was employed, the coarse columnar β grains transformed into short columnar and equiaxed grains. With the increased of interpass milling depth, the average size of α phase was gradually refined to 13.5 μm below. The highest average microhardness in the top, middle and bottom areas obtained by using the interpass milling depth of 300 μm were 369 HV 0.2 , 371 HV 0.2 and 371 HV 0.2 respectively, which was increased by 32 HV 0.2 , 28 HV 0.2 and 26 HV 0.2 compared with non-interpass milling respectively. The horizontal and vertical ultimate tensile strength first increases and then decreases with the increase of interpass milling depth, reaching its maximum at a milling depth of 300 μm. The highest tensile strength of the horizontal and vertical directions obtained by using the interpass milling depth of 300 μm were 1022 MPa and 1042 MPa. The level of the ultimate tensile strength is related to the combined proportion of total average β grain size and total average <15 μm α phase size, and the proportion of both is balanced and maximized to obtain the maximum ultimate tensile strength. The interpass milling depth of 300 μm satisfies both conditions, so its maximum horizontal and vertical ultimate tensile strength is achieved. Fracture type of tensile specimen was ductile fracture due to observing a lot of dimples on the fracture morphology. The above conclusions show that interpass milling is an aided process to effectively improve the microstructure and mechanical properties of TC4 titanium alloy GTAW wire arc additive manufacturing thin-walled parts, which has high research significance and practical value.

Grain Morphology Evolution and Texture Characterization of Wire and Arc Additive Manufactured Ti-6Al-4V

Weakening the Anisotropic Property and Refining Prior-β Grains via Hammer Peening Treatment During Wire Arc Additively Manufacturing of Ti-6Al-4V

Modification of α-phase of wire + arc additive manufactured Ti-6Al-4 V alloy with boron addition

The Effect of Thermal History on Microstructural Evolution, Cold-Work Refinement and α/\b{eta} Growth in Ti-6Al-4V Wire + Arc AM

Controlling the Microstructure and Properties of Ti-6.5al-2zr-1mo-1v Components Fabricated by High-Deposition-Rate Wire Arc Additive Manufacturing

Fabrication of γ-TiAl intermetallic alloy using the twin-wire plasma arc additive manufacturing process: Microstructure evolution and mechanical properties

Microstructure evolution and mechanical properties of the wire + arc additive manufacturing Al-Cu alloy

Microstructure regulation of titanium alloy functionally gradient materials fabricated by alternating current assisted wire arc additive manufacturing

Microstructural evolution and mechanical characterization of wire arc additively manufactured 2Cr13 thin-wall part

Research on high efficiency deposition method of titanium alloy based on double-hot-wire arc additive manufacturing and heat treatment

Improvement of Microstructure and Mechanical Properties of TC4 Titanium Alloy GTAW based Wire Arc Additive Manufacturing by using Interpass Milling

Effect of Cu content on microstructure and properties of Ti-6Al-4V alloy fabricated by double-wire arc additive manufacturing

Achieving a Columnar-to-Equiaxed Transition Through Dendrite Twinning in High Deposition Rate Additively Manufactured Titanium Alloys

Additive manufacturing of Ti-6Al-4V alloy by micro-laser metal wire deposition with pulsed wave emission: processability and microstructure formation

Simulation of solidified <i></i> grain for Ti-6Al-4V during wire laser additive manufacturing by three-dimensional cellular automaton method

Effects of synchronized magnetic arc oscillation on microstructure, texture, grain boundary and mechanical properties of wire arc additively manufactured Ti6Al4V alloy

Enhancement of Microstructural and Tensile Isotropy for Ti–6Al–4V and Ti–6Al–2Sn–2Zr–2Mo–2Cr Alloys Deposited with Wire Arc Additive Manufacturing and Interlayer Peening

Mechanical and tribological characterization of wire and multi-wire arc additive manufactured thin-walled TC11 component

Effects of Heat Accumulation on the Arc Characteristics and Metal Transfer Behavior in Wire Arc Additive Manufacturing of Ti6Al4V

Regionalization of microstructure and mechanical properties of Ti6Al4V transition area fabricated by WAAM-LMD hybrid additive manufacturing

Microstructure and Mechanical Properties of TiB2/AlSi7Mg0.6 Composites Fabricated by Wire and Arc Additive Manufacturing Based on Cold Metal Transfer (WAAM-CMT)