Abstract:Size-tunable beta-NaYF4: Yb/Er (50-400 nm) up-converting nanoparticles (UCNPs) with a strong green emission were successfully prepared by a facile thermal decomposition method in a short period of time. The effects of the reaction time, the oleic acid (OA) content, and the doped Gd3+ concentration on the crystal structure, the size evolution mechanism and the luminescence mechanism of the beta-NaYF4: Yb/Er nanoparticles were discussed in detail. Characterization was completed using X-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution (HR-TEM), scanning electron microscopy (SEM), and photoluminescence (PL). The results reveal that the phase transition was completed at 15 min and the morphology of the NaYF4: Yb/Er UCNPs changed from spherical to large hexagonal disks (200-400 nm) in non-doped Gd3+. An appropriate decrease in the volume ratio of oleic acid (OA) to 1-octadecene (ODE) promoted NaF production, resulting in the formation of the hexagonal phase crystals and the subsequent increase of luminous intensity by 30-40 times. More importantly, the size of the beta-NaYF4: Yb/Er decreased with Gd3+ doping, and the UCNPs ultimately transformed into small hexagonal prisms (50 nm) with high monodispersity when the doping concentration of Gd3+ was 60 mmoL. The PL spectra confirmed that the luminous intensity of the UCNPs with doped Gd3+ was much higher than that of the undoped UCNPs. The results show that this route for UCNP fabrication with high luminous efficiency and a small size could be extended to other UCNP systems for multifunctional biomedical applications.

Facile Synthesis, Morphology Evolution and Tunable Luminescence of NaGdF4:Yb,Er Nanorods with Various Aspect Ratios

Controllable Synthesis, Upconversion Luminescence, and Paramagnetic Properties of Nagdf4:Yb3+,Er3+ Microrods

Synthesis, Phase Structure and Up-Conversion Luminescence of Nayf4:Yb3+, Er3+/Tm3+ Nanorods

Na(Y<sub>1.5</sub>Na<sub>0.5</sub>)F<sub>6</sub>Single-Crystal Nanorods as Multicolor Luminescent Materials

Na(Y1.5 Na0.5)F6 single-crystal nanorods as multicolor luminescent materials.

Rare earth doped NaYF 4 nanorods: Synthesis and up-conversion luminescence spanning deep-ultraviolet to near-infrared regions

Crystalline Phase and Morphology Controlling to Enhance the Up-Conversion Emission from NaYF4:Yb,Er Nanocrystals

Size-tunable Β-Nayf4:Yb/er Up-Converting Nanoparticles with a Strong Green Emission Synthesized by Thermal Decomposition

Controlled Synthesis and Luminescence of Lanthanide Doped NaYF<sub>4</sub>Nanocrystals

Controlled Synthesis and Luminescence Properties of Β-Nagdf4: Yb3+, Er3+ Upconversion Nanoparticles

Synthesis and Luminescence Properties of Water Soluble α-NaGdF4/β-NaYF4:Yb,Er Core-Shell Nanoparticles

Improved Upconversion Luminescence Properties of Gd2O3:Er3+/Gd2O3:Yb3+ Core-Shell Nanorods.

Controllable Synthesis and Upconversion Luminescenceof NaYF4:Yb3+, Er3+ Nanocrystals

Controlled Growth along Circumferential Edge and Upconverting Luminescence of Β-Nayf4: 20%yb3+, 1%er3+ Microcrystals

Hydrothermal Synthesis and Aspect Ratio Dependent Upconversion Luminescence of NaYF4:Yb3+/Er3+ Microcrystals.

Tin-(IV) dopant-controlled synthesis of Yb3+/Er3+:NaGdF4 nanocrystals: Morphology transformation and intensified upconversion performance

Hexagonal NaYF4:Yb3+/Er3+ Nano/micro-Structures: Controlled Hydrothermal Synthesis and Morphology-Dependent Upconversion Luminescence

Synthesis of Upconversion β-NaYF₄:Nd 3+ /Yb 3+ /Er 3+ Particles with Enhanced Luminescent Intensity through Control of Morphology and Phase.

Hexadecylpyridinium Chloride Mediated Hydrothermal Synthesis of NaYF₄:Yb, Er Nanocrystal and Their Luminescent Properties

Enhanced up-conversion luminescence from NaYF4:Yb,Er nanocrystals by Gd3+ ions induced phase transformation and plasmonic Au nanosphere arrays

Morphology control and upconversion luminescence enhancement of Na1-xLixY.78-yLuyF4:Er.02Yb.2 microcrystals by doping ions with different valences