Abstract:In this experimental investigation, a core–shell-structured nano-lubricating additive was synthesized utilizing the dielectric barrier discharge plasma (DBDP)-assisted ball grinding technique for a duration of 5 h. The microstructural analysis of the nano-TiO2 powder was performed employing advanced methods such as X-ray diffraction (XRD) and thermogravimetry–differential scanning calorimetry (TG-DSC). The initial particle size of TiO2 was refined from 1 μm to a range of 150–200 nm, resulting in a remarkable increase in lattice distortion rate by 88.2% and an oil affinity enhancement of 200%. Through the introduction of CTAB’s oil-compatible group onto the surface of nano-TiO2 particles, a modified layer with a thickness of 21 nm possessing superior thermal stability and an activation energy (E a) of 600 kJ/mol was successfully produced. Molecular dynamics simulations were conducted to elucidate the mechanism underlying the surface modification of nano-TiO2 powder facilitated by DBDP-assisted ball grinding, thereby revealing the pivotal role of electrostatic forces in the organic modification of the TiO2 surface. It was found that electrostatic forces dominantly govern the cetyl trimethyl ammonium bromide (CTAB)–TiO2 composite interface model, contributing to 70% of the total energy with a maximum energy proportion of −187.84 kcal/mol. To evaluate the lubrication performance of the composite oil samples under boundary lubrication conditions, comprehensive assessments were carried out using the four-ball method and reciprocating friction experiments. The results demonstrated noteworthy enhancements in viscosity index, dynamic viscosity, and oil film thickness within the composite oil samples. Particularly, the composite oil containing 0.5 wt % TiO2@CTAB exhibited outstanding extreme pressure resistance, manifesting a significant reduction of 41.7% in the average friction coefficient, a considerable increase of 25.8% in wear spot diameter, and a substantial elevation of 66.9% in maximum nonseizure load. Compared to the base oil, the incorporation of 0.5 wt % TiO2@CTAB led to a notable increment of 34.7% in oil film thickness, 6.7% in dynamic viscosity, and 9% in viscosity index. In the tribological experiment simulating marine diesel engines, the friction coefficient witnessed a remarkable reduction by 65.8%, accompanied by a substantial decrease of 54.1% in wear rate. This noteworthy improvement in boundary lubrication conditions of the friction pair effectively mitigated friction and wear. For comprehensive characterization of the wear marks, energy-dispersive spectrometry (EDS) and X-ray photoelectron spectroscopy (XPS) techniques were employed to analyze the physical structure and chemical composition. The implementation of TiO2@CTAB nano-lubricating additives resulted in nanobearing and deposition effects, leading to a reduction in contact area and surface roughness, thereby facilitating the restoration of the friction pairs. These findings possess significant implications for extending the service life of diesel engines and ensuring safe navigation. Furthermore, these studies underscore the considerable potential of core–shell-structured TiO2@CTAB for widespread application in diesel engines.

Well Dispersive TiO2 Nanoparticles As Additives for Improving the Tribological Performance of Polyalphaolefin Gel Lubricant

Effect of the Combination of Antioxidant and Dispersant in Traction Oils on Their Interactions and Lubricating Property

Tribological Properties of Polyalphaolefin (PAO6) Lubricant Modified with Particles Additives of Metallic Glass

Adsorption-Enhanced Friction Reduction in TiN-Ag/polyalphaolefin (PAO) Solid-Liquid Systems: Catalytic Induction of Amorphous Carbon Formation

Adaptive TiN-Cu/PAO Composite Lubrication System: the Tribocatalysis-induced PAO6 Transferring to Amorphous Carbon

Effect of TiO2 nanoparticles on the tribological properties of lubricating oil: an experimental investigation

Friction-reduction and Anti-Wear Properties of Polyalphaolefin Oil with Mo-DTC Additive Enhanced by Nano-Carbon Materials

Alkyl Titanate-Modified Graphene Oxide as Friction and Wear Reduction Additives in PAO Oil

Iron phosphate nanoparticles as oil additives to enhance anti-wear properties

Poly(Tannic acid)-Functionalized Onion-like Carbon Nanoparticles Derived from Candle Soot Serving as Potent Lubricant Additives

Stable and Durable TiBN-Cu/polyalphaolefin(PAO) Composite Lubrication System: Enhanced Lubrication Performance Through PAO Physicochemical Adsorption

Tribological Properties of TiO 2 @CTAB Core–Shell Nanopowders as Lubricating Additives

The Tribological Mechanism of Cerium Oxide Nanoparticles as Lubricant Additive of Poly-Alpha Olefin

Insight into the tribological performance and mechanisms of MoN-Ag/oil solid-liquid lubrication system based on catalytic effect

Tribological Properties of Polydopamine-Modified Ag As Lubricant Oil Additives

Tribological effects of oxide based nanoparticles in lubricating oils

Performance and Anti-Wear Mechanism of CaCO3 Nanoparticles As a Green Additive in Poly-Alpha-olefin

Preparation and tribological behaviors of magnesium silicate hydroxide-MoS2 nanoparticles as lubricant additive

Tribological Study of Oil-Miscible Quaternary Ammonium Phosphites Ionic Liquids as Lubricant Additives in PAO

Improving the lubricating performance of poly-alpha-olefin base oil using SnO2 nanosized-additives

TiO 2 and CeO 2 nanoparticles as lithium complex grease additives for enhanced lubricity