Microstructure Evolution and Enhanced Fracture Toughness of Ti-44Al-8Nb-0.1B Alloy Fabricated by Cold Crucible Directional Solidification under Different Temperature Gradients
Shulin Dong,Qi Wang,Ruirun Chen,Yingdong Qu,Jingjie Guo,Guanglong Li,Wei Zhang,Bo Yu
DOI: https://doi.org/10.1016/j.matchar.2022.112591
IF: 4.537
2023-01-01
Materials Characterization
Abstract:In order to clarify the effect of temperature gradient on microstructure of high-Nb TiAl-based alloy prepared by cold crucible directional solidification (CCDS), clarify the effect of the CCDS microstructure on fracture toughness, and finally improve the fracture toughness of high-Nb TiAl-based alloy, we chose the Ti-44Al-8Nb-0.1B alloy, prepared the alloy ingots by CCDS at fixed solidification rate but different input powers (temperature gradients). The results show that, with the input power increasing, the temperature gradient also increases. At lower input powers of 35, 40, 45 kW, we can only obtain the equiaxed grain (lamella colony) dominated microstructure, and the corresponding fracture toughness is not much improved. At higher input powers of 48, 50 kW, it is more easily to obtain the directional solidification microstructure, including aligned lamella colonies, higher percentage of small-angle lamellas, and a new type "banded microstructure". The directional solidifica-tion microstructure can significantly improve the fracture toughness, and the fracture toughness of the alloy prepared at 50 kW is the best, up to 35.33 MPa center dot m(1/2), corresponding to the "banded microstructure". How the input powers (temperature gradients) affect the CCDS macro/microstructure, and how the CCDS macro/ microstructure affects the fracture toughness are discussed. Since the "banded microstructure" exhibits an excellent fracture toughness, we study and clarify how this microstructure can be obtained: firstly, the (110)beta basal plane preferred orientation (texture) should be obtained; secondly, a high input power (temperature gradient) should be provided to supply more energy for the long-distance growth of the subsequent alpha phase and gamma phase along the direction of directional solidification.