Abstract:A novel quasi-continuous network reinforced structure that consists of borides and carbides in B4C/TiAl matrix composites was innovatively designed for the strengthening at high temperatures. Simultaneously, impacts of such reinforced structures on microstructures and mechanical properties of the composites have been unveiled. TiAl matrix units in B4C/TiAl composites are duplex microstructures which are composed of (alpha 2+gamma) colonies and gamma grains. The ascent of B4C contents triggers off the formation of network reinforced structures in the layers of TiAl matrix units. With B4C contents increasing to 0.1 wt%, elasticity modulus and ultimate compressive strengths of B4C/TiAl composites are upgraded from 10.944 GPa and 723.10 MPa to 16.052 GPa and 774.611 MPa. As B4C contents reach at 5.0 wt%, elasticity modulus and ultimate compressive strengths further soar to 17.244 GPa and 799.19 MPa. Borides and carbides within the quasi-continuous network reinforced structures are unfolded as stripe and needle shaped TiB with B27 structure and Ti2AlC particles with MAX structure. Parts of Ti2AlC particles take TiB as cores to nucleate and grow. Moreover, TiC phases usually act as the cores for the nucleation of Ti2AlC particles. The orientation relationships of such reinforcements represent as [011]TiC// [010]TiB, (1-11)[011]TiC//(0006) [-2110]Ti2AlC, [100]TiB//[0001]Ti2AlC, [010]TiB//[-2110]Ti2AlC and [001]TiB// [01-10]Ti2AlC. The fractures of TiB are usually along or perpendicular to [010]TiB direction. Meanwhile, the fracture surfaces of TiB are always parallel to (100)TiB or (010)TiB planes. Additionally, dislocations slip through Ti2AlC particles and lead to separation and sliding of staking planes (0001)Ti2AlC within Ti2AlC lattices. TiB and Ti2AlC with alternative distribution can stabilize the network reinforced structures and upgrade properties of B4C/TiAl composites.

Structural Design of Laminated B4C/TiC Composite Fabricated by Reactive Melt Infiltration

Microstructure and Wear-resistant Properties of in situ TiB-TiC Reinforced Titanium Matrix Composites by Laser Deposition Manufacturing

Fabrication of Fully Dense Tial-Based Composite Sheets with A Novel Microlaminated Microstructure

Interfacial Reactions and Mechanical Properties Studies of C-Coated and C/B4C Duplex-Coated SiC Fiber-Reinforced Ti2AlNb Composites

Microstructural Characteristics of Reaction-Bonded B4C/SiC Composite

Microstructures and mechanical properties of in-situ SiC-TiB2 ceramic composites fabricated by reactive melt infiltration

Microstructure and Mechanical Properties of Multi-Carbides/(al, Si) Composites Derived from Porous B4C Preforms by Reactive Melt Infiltration

Fabrication of (Tib/ti)-Tial Composites with a Controlled Laminated Architecture and Enhanced Mechanical Properties

Fabrication and mechanical properties of TiB w /Ti-Ti(Al) laminated composites

Design and Thermodynamics of In-Situ TiB2 Reinforced B4 C Matrix Composites

Mechanical Properties of (ti2alc+ti3alc)–tial Ceramic–intermetallic Laminate (CIL) Composites

Microstructure and compressive properties of in situ synthesized (TiB + TiC)/Ti composites

Study Of Multi-Carbide B4c-Sic/(Al, Si) Reaction Infiltrated Composites By Sem With Ebsd

Microstructure and Mechanical Properties of TiBw/Ti-Ti3Al Metal-Intermetallic Laminate (MIL) Composites

Microstructures and Mechanical Properties of TiAl Matrix Composites with Multi-Precipitates Quasi-Continuous Network Reinforced Structures

The Microstructure Evolution of TC4-(TiB + TiC)/TC4 Laminated Composites by Laser Melting Deposition

TEM Characterization of Symbiosis Structure of in Situ TiC and TiB Prepared by Reactive Processing of Ti–B4C

Fabrication and characterization of laminated Ti-(TiB+La 2 O 3 )/Ti composite

Fabrication and characterization of in-situ TiAl matrix composite with controlled microlaminated architecture based on SiC/Al and Ti system

Fabrication Of Tial Matrix Composite Sheetes With Controlled Micro-Laminated Architecture By A Solid-Liquid Reaction

Novel Α/β SiC-(Ti, Nb)B2 Toughened (ti, Nb)C-based Composites with Enhanced Mechanical Properties Fabricated by in Situ Reactions Sintering at Low Temperature