Plasticity of Laser-Processed Nanoscale AlAl2Cu Eutectic Alloy

S. J. Wang,G. Liu,D. Y. Xie,Q. Lei,B. P. Ramakrishnan,J. Mazumder,J. Wang,A. Misra

DOI: https://doi.org/10.1016/j.actamat.2018.06.038

IF: 9.4

2018-01-01

Acta Materialia

Abstract:Deformation behavior of as-cast and laser re-melted AlAl2Cu eutectic alloys subjected to room temperature rolling was investigated by transmission electron microscopy. For as-cast alloys, with inter-lamellar spacing of a few micrometers, Al2Cu layers exhibit brittle behavior but plastic co-deformation was observed in rolled, laser processed nanoscale alloys. The nanoscale Al2Cu lamellae, constrained by nanoscale Al, deform via defects not previously reported in monolithic Al2Cu intermetallic: localized shear on {011}Al2Cu planes and shear-induced faults on {121}Al2Cu planes. Based on crystallographic analysis of slip continuity across the interface, the unexpected plasticity mechanisms are ascribed to the slip continuity across interface between α-Al and θ-Al2Cu layers associated with the orientation relationship in AlAl2Cu eutectics. The difference in shear mechanisms on the two planes is attributed to low energy faulted structures associated with shear on {011}Al2Cu and {121}Al2Cu planes, as examined by first-principles density functional theory calculations. These findings demonstrated that nanoscale microstructures promote plastic co-deformation in metallic composites with soft and hard phases.