Abstract:The acid properties of BEA/MOR (intergrowth of zeolite beta and mordenite) samples with SiO2/Al2O3 molar ratio of 25 were characterized by temperature-programmed desorption of NH3(NH3-TPD),. There is a volcano-type relationship between the higher NH3-TPD peak temperature and the mordenite content of the BEA/MOR samples, and the NH3-TPD peak temperature reached the maximum at mordenite content of about 65%. In contrast, there is a linear relationship between the higher NH3-TPD peak temperature and the mordenite content of the mechanical mixtures of zeolite P and mordenite. No obvious difference in the acid strength existed between the BEA/MOR samples and the mechanical mixtures when the mordenite content was less than 50%. However, when the mordenite content exceeded 50%, the BEA/MOR samples possessed much higher acid strength than the mechanical mixtures. The BEA/MOR sample with 65% mordenite showed the highest acid strength, which was higher than that of the mordenite. The catalytic activity measurements of all the samples for methanol dehydration were carried out in a fixed-bed reactor under atmospheric pressure, temperature of 180 degrees C, and methanol space velocity of 2 h(-1). Dimethyl ether and water were the only products for each catalyst. No coke formation and catalyst deactivation were observed in the reaction of 6 h. There is a linear relationship between the methanol conversion and the mordenite content of the mechanical mixtures. The BEA/MOR samples with mordenite content higher than 40% showed higher catalytic activity than HM, and the BEA/MOR with 65% mordenite showed the highest methanol conversion. The catalytic activity of BEA/MOR also exhibited a volcano-type behavior. Compared with the mechanical mixtures, the BEA/MOR samples displayed higher catalytic activity. The HM with SiO2/Al2O3 molar ratio of 11 deactivated after 60 h reaction though it had high initial activity. The HBEA/MOR with SiO2/Al2O3 molar ratio of 53 showed relatively high catalytic activity and stability.

The Influence of Dealumination Methods on the Properties of Mordenites

On the Hydrophobicity of Mordenite

INFLUENCE OF SILICA SOURCE ON THE CRYSTALLIZATION OF MORDENITE ZEOLITE

Preparation of Mordenite Composite Membranes with Seeding

Influence of the treatment of mordenite by ammonium hexafluorosilicate on physicochemical and catalytic properties

Highly water-selective mordenite membranes prepared via hydrothermal post-treatment in a dilute hydrochloric acid solution

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

Preparation of Highly Water-Selective Mordenite Membranes Via Post-Synthetic Treatment with Oxalic Acid

Textural characterization of zeolites with complex pore systems: The case of dealuminated mordenite zeolites

MAS NMR Studies on the Dealumination of Zeolite MCM-22

Impact of Various Silicon Sources on the Synthesis of Mordenite and Differences in the Carbonylation Reaction of Dimethyl Ether

Controlling Crystal Transformation Between Zeolite Zsm-5 and Mordenite Without Organic Structure-Directing Agent

PREPARATION AND PROPERTIES OF A NEW KIND OF ACID CATALYST OF ZEOLITE COATING ON METAL-SURFACE

Influence of cations (Li+, Na+, K+)for synthesis mesoporous molecular sieve MCM-41 and their properties

Effect of dealumination defects on the properties of zeolite Y

In-Situ Ir Monitoring Of The Acidic And Structural Variations Of Mordenite Caused By Pressure And Temperature

On the Acid-Dealumination of USY Zeolite: a Solid State NMR Investigation

Modelling of Dealumination of Silicon-Aluminum Molecular Sieves

Acidity and Catalytic Performance of BEA/MOR Intergrowth Zeolites

Influence of lanthanum modified mordenite on alkylation of toluene with methanol

On understanding the sequential post-synthetic microwave-assisted dealumination and alkaline treatment of Y zeolite