Abstract:To study the mechanism of the photo-thermochemical cycle (PTC), titanium dioxide (ST) and Ni-doped TiO2 (NT) films were produced using a sol-gel method and applied in the PTC for CO2 reduction. And commercial P25 (PT) has been used as a compared sample. A comparison of CO production shows that Ni-doped TiO2 performed better than undoped TiO2 and P25. Average CO production of NT PTCs was 5.30 punolig-cat and it was nearly 3.13 times of ST PTCs' CO production and 2.28 times of PT PTCs'. Scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy -dispersive X-ray spectroscopy (EDXS) and X-ray diffraction (XRD) were used to assess the crystal structure and morphology of the films. Ni element could be found in NT by EDXS and inductively coupled plasma-atomic emission spectrometry (ICP-AES), and the mass fraction of Ni was 0.54% and 0.436% which were agreed with experiments. This result of XRD indicated that Ni2+ may have high dispersion without significant change in TiO2 and Ni2+ ions were doped into the TiO2 lattice so that Ni-O-Ti bonds were formed. Photoluminescence (PL), time-resolved PL, UV-visible diffuse reflectance spectra (UV-visible DRS) and X-ray photoelectron spectroscopy (XPS) analyses were also conducted to investigate the charge transfer and reaction mechanisms on the sample surface. The incorporation of Ni into TiO2 resulted in a weaker PL intensity than that of bare TiO2, which suggests that the introduction of Ni into TiO2 effectively suppressed the undesirable recombination of electrons and holes. According to UV-visible DRS results, the E, of PT is approximately 3.07 eV, which is smaller than that of ST (E-g=3.23 eV) and PT (E-g= 3.20 eV). The narrower band gap of NT indicates that NT absorbed light with a wider wavelength range than that absorbed by ST and PT. By XPS patterns, the increase of Ni+/0 and Ti3+ indicated that the Vo may have been produced on the bond of Ni-O-Ti after UV illumination, and oxygen vacancies (Vo) have been consumed after thermal step in PTC. Density functional theory (DFT) calculations related to the anatase (101) surface of TiO2 and Ni doped TiO2 was performed to verify and provide guidance for enhancing the PTC mechanism. Single and second Vo formation energy have been calculated. The Ni-doped surface exhibits better performance than the undoped surface in the first step in PTC, because of its lower Vo formation energy which produce more Vo sites. Density of states (DOS) and partial density of states (PDOS) results indicated that narrow energy gap and impurity energy level of Ni-doped TiO2 may lead to a wider wavelength range of NT. As a result, several key factors of the mechanism have been clarified.

Photothermal Coupling Factor Achieving CO2 Reduction Based on Palladium-Nanoparticle-Loaded TiO2

Visible Light-Responding Perovskite Oxide Catalysts for Photo-Thermochemical CO2 Reduction

Efficient CO2 Reduction with H2O Via Photothermal Chemical Reaction Based on Au-MgO Dual Catalytic Site on TiO2

Photothermal Catalysis: Photothermal Catalyst Engineering: Hydrogenation of Gaseous CO2 with High Activity and Tailored Selectivity (adv. Sci. 10/2017)

Guiding Effective Nanostructure Design for Photo-Thermochemical CO2 Conversion: from DFT Calculations to Experimental Verifications

Accelerating Photoelectric CO2 Conversion with a Photothermal Wavelength-Dependent Plasmonic Local Field

Photothermal Catalysis for Selective CO2 Reduction on the Modified Anatase TiO2 (101) Surface

Enhanced Solar Conversion of CO2 to CO Using Mn‐doped TiO2 Based on Photo‐thermochemical Cycle

Photo-thermochemical Cycle for CO2 Reduction Based on Effective Ni Ion Substitute-doped TiO2

Atomic Interface Engineering of Single‐Atom Pt/TiO2‐Ti3C2 for Boosting Photocatalytic CO2 Reduction

Photocatalytic Reduction of Carbon Dioxide to Methane at the Pd-Supported TiO 2 Interface: Mechanistic Insights from Theoretical Studies

Remarkable CO 2 photoreduction activity using TiO 2 nanotube arrays under favorable photothermal conditions driven by concentrated solar light

Selective catalytic photoreduction of CO 2 on Pt/TiO 2 nanotube for renewable energy

Photoelectrocatalytic Reduction of CO2 to CO via Cu2O/C/PTFE Nanowires Photocathodes

Enhanced Photocatalytic Performance Toward CO2 Hydrogenation over Nanosized TiO2-Loaded Pd under UV Irradiation

Selective photocatalytic CO2 reduction in aerobic environment by microporous Pd-porphyrin-based polymers coated hollow TiO2

Efficient Electron Transfer in g-C3N4/TiO2 Heterojunction for Enhanced Photocatalytic CO2 Reduction

Thermoplasmonic TiN boosts photocatalysis in covalent-organic frameworks

Boosting photo-thermal co-catalysis CO2 methanation by tuning interface electron transfer via Mott-Schottky heterojunction effect

Enhancing the photoelectrochemical performance of TiO2 photoanode by employing carbon nanoparticles as electron reservoirs and photothermal materials

Particle Size-Dependent Charge Transfer Dynamics for Boosting CO2 Photoreduction over Ag/TiO2 Heterojunction