Abstract:Diffusion bonding of additive manufactured (AM) metal parts to traditionally manufactured metal parts could simultaneously achieve large-scale, complex-structure, and multi-material parts. However, there is a lack of study on diffusion bonding as well as its interface formation mechanism between AM metal parts and traditionally manufactured metal parts. In this study, diffusion bonding was performed to join AM 316L stainless steel and casting 45 steel at different temperatures. The element distribution, interface characteristics and shear strength of the joints were investigated, and the interface formation mechanism at different bonding temperature was analyzed in detail. The results reveal that the interface transition zone from the AM 316L steel side to the 45 steel side is composed of the metallic elements diffusion layer and the carbide layer. Moreover, an increase in bonding temperature can effectively promote interface voids closure and increase the thickness of the metallic elements diffusion layer, while the thickness of the carbide layer firstly increases and then decreases as the temperature increases. The component of the carbide layer was identified as brittle compounds (CrFe)23C6 and (CrFe)7C3. The shear strength of the joints exhibited an increasing trend with the increasing bonding temperature. Interestingly, a sudden decrease in strength was found at 950 °C due to the significant increase of the brittle carbide layer, while high-quality joints could be achieved as the brittle carbides dissolve at 1000 °C. This study could lay the foundation for understanding diffusion bonding interface behaviors between AM metal parts and traditional casting metal parts.

Corrosion of the Bonding at FeCrAl/Zr Alloy Interfaces in Steam

Study on interface behavior of Be/CuCrZr alloy by diffusion bonding

Investigation on the Oxidation and Corrosion Behaviors of FeCrZr Alloy As a Protective Material for Zr Cladding

Microstructure of FeCrAl Thin Film Composed of Nanocrystals Deposited on Zr Alloy and Their Corrosion Behavior under Water Steam Atmosphere.

Improved oxidation resistance of Cr/FeCrAl coating on Zr alloy in high-temperature steam environment

Interface Behaviors and Mechanical Properties of Diffusion Bonded 45 Steel/additive Manufactured 316L Steel Joints

Xe20+ ions irradiation and autoclave corrosion coupled with steam oxidation behaviors of FeCrAlMoSiY-coated Zr claddings

Effect of Cr/Al Atomic Ratio on the Oxidation Resistance in 1200°C Steam for the CrAlSiN Coatings Deposited on Zr Alloy Substrates

Evolution of Cr/Cr2O3 interface in Cr-coated zirconium alloy in high temperature steam

Corrosion of Zr-Sn-X (X: Fe, Ni or Cr) Ternary Alloy in High Pressure Steam at High Temperature

Incipient Corrosion of FeCrAl Alloys in H3BO3- and LiOH-containing Pure Water at 360 °C and 18.5 MPa

Study on the corrosion mechanism of Zr-1Sn- x Fe-0.2Cr-0.02Ni alloy in 500 °C super-heated steam with oxygen

Corrosion of New Zirconium Claddings in 500 °C/10.3 MPa Steam: Effects of Alloying and Metallography

Oxidation Resistance Improvement of Zr-4 Alloy in 1000 °C Steam Environment Using ZrO2/FeCrAl Bilayer Coating

Effect of Diffusion Barriers on Steam Oxidation Properties and Interface Evolutions of Cr Coating for Zirconium Alloy at 1200 °C

Effects of Alloyed Si on the Autoclave Corrosion Performance and Periodic Corrosion Kinetics in Zr–Sn–Nb–Fe–O Alloys

Bonding and wear behaviors of supersonic plasma sprayed Fe-based coatings on Al-Si alloy substrate

High-temperature steam oxidation behavior and failure mechanisms of Al alloyed Cr coatings on Zr-4 alloy

Corrosion Behavior of Nb-doped FeCrAl Alloy in 500°C Steam

Systematic investigations on the oxidation mechanism of Cr coated Zr-4 alloy under different high-temperature steam conditions

Systematic investigation of the oxidation behavior of Fe-Cr-Al cladding alloys in high-temperature steam