Abstract:Purpose Solder bumps for chip interconnections are downsizing from current approximately 100 μm to the expected 1 μm in future. As a result, the Cu-Ni cross-interaction in Cu/Solder/Ni solder joints will be more complicated and then strongly influence the growth of the intermetallic compounds (IMCs). Thus, it is critical to understand the fundamental aspects of interfacial reaction in micro solder joints. This paper aims to reveal the effect mechanism of reflow temperature and solder size on the interfacial reaction in Cu/Solder/Ni solder joints. Design/methodology/approach The Cu-Ni cross-interaction in the Cu/Sn/Ni micro solder joints with 50 and 100 μm solder sizes at 250°C and 300°C were observed, respectively. The line-type interconnects were soaked in silicone oil, and the temperature of the line-type interconnects was 250 ± 3°C and 300 ± 3°C, which were monitored by a fine K-type thermocouple, and followed by an isothermal aging process at various times. After aging, the specimens were removed from the silicone oil and cooled in the air to room temperature. Findings The major interfacial reaction product on both interfaces was (Cu,Ni) 6 Sn 5 , and the asymmetric growth of (Cu,Ni) 6 Sn 5 , evidenced by the thickness of (Cu,Ni) 6 Sn 5 IMCs at the Sn/Ni interface was always larger than that at the Sn/Cu interface, resulted from the directional migration of Cu atoms toward the Sn/Ni interface under Cu concentration gradient. The morphology of (Cu,Ni) 6 Sn 5 IMC at Sn/Cu interface was columnlike at 250°C, and which changed from columnlike to scallop with large aspect ratio at 300°C, while that at Sn/Ni interface gradually evolved from needlelike to the mixture of needlelike and layered at 250°C, and which evolved from needlelike to scallop with large aspect ratio at 300°C. The evolution of morphology of (Cu,Ni) 6 Sn 5 is attributed to the content of Ni. Furthermore, the results indicate that the Cu-Ni cross-interaction was stronger with small solder size and relatively low temperature in the Cu/Sn/Ni micro solder joints. Originality/value The asymmetric growth of (Cu,Ni) 6 Sn 5 in the Cu/Sn/Ni micro solder joints, evidenced by the thickness of (Cu,Ni) 6 Sn 5 IMCs at the Sn/Ni interface, was always larger than that at the Sn/Cu interface. The morphology evolution of (Cu,Ni) 6 Sn 5 IMC at both interfaces was attributed to the content of Ni. The Cu-Ni cross-interaction was stronger with small solder size and relatively low temperature in the Cu/Sn/Ni micro solder joints.

Interfacial Compounds Characteristic and Its Reliability Effects on SAC305 Microjoints in Flip Chip Assemblies

Size Effect of IMC Growth in Liquid-Solid Reflow Reaction at SAC305/Cu Interface

Effect of the Cross-Interaction on the Formation and Evolution of Intermetallic Compounds in Cu(Ni)/Sn-Ag-Cu/Cu(Ni) Bga Structure Solder Joints

Effect of reflow temperature and solder size on Cu-Ni cross-interaction in the Cu/Sn/Ni micro solder joints

Study on the Interfacial IMCs Growth of Nt-Cu/in Solder Joints

Quasi In-Situ Study Of Morphological Evolution Of The Interfacial Imc In Single-Sided Interface Sn-0.3ag-0.7cu/Cu Joints During Multiple Reflow Process

Effect of Sn Surface Diffusion on Growth Behaviors of Intermetallic Compounds in Cu/ni/snag Microbumps

A Study of the $\mu$ -Solder Joint on Ajinomoto Build-up Film Using the Solder on Pad (SOP) Process for Multi-Chip Module

Growth behavior and morphology evolution of interfacial (Cu,Ni)6Sn5 in (001)Cu/Sn/Ni micro solder joints

Effects of Joint Height on the Interfacial Microstructure and Mechanical Properties of Cu-Cored SAC305 Solder Joints

Reliability Improvement of SnAgCu Interconnections under Extreme Temperature Condition by TiO2 Nanoparticles Doping: Experiments and First Principles Calculations

Solder Size Effect on Interfacial Reaction and Growth Behavior of Cu–Sn Intermetallic Compounds in Cross-Scale Sn3.0Ag0.5Cu/Cu Joints Between Stacking TSV Chips During Step-Reflow Processes

Interfacial Reactions Between Sn-Cu Solder Alloy and Cu/Ni Coatings During Reflow Soldering

Study on the dual inhibition behavior of interfacial IMCs in Cu/SAC105/Cu joint by adopting SiC nanowires and nanocrystalline Cu substrate

Growth kinetics of (Cu<sub>x</sub>Ni<sub>1-x</sub>)<sub>6</sub>Sn<sub>5</sub> intermetallic compound at the interface of mixed Sn63Pb37/SAC305 BGA solder joints during thermal aging test

Size and Constraint Effects on Interfacial Fracture Behavior of Microscale Solder Interconnects.

The Growth of Interfacial IMC Layer in SAC0307 Solder Joints with Specific Grain Orientation Under Electrical and Thermal Coupling Fields

Cross-Interaction of Interfacial Reactions in Ni (Au/ni/cu)-Snag-cu Solder Joints During Reflow Soldering and Thermal Aging

Grain modification and formation of tough IMC phase in submicron Sn–Ag microbumps via doping Zn and Ni in Cu substrate

Microstructural evolution of Cu–Sn–Ni compounds in full intermetallic micro-joint and in situ micro-bending test

Interfacial Intermetallic Compound Growth in Sn-3Ag-0.5Cu/Cu Solder Joints Induced by Stress Gradient at Cryogenic Temperatures