Abstract:The size effect in the fracture of solids represents a highly critical issue with a prolonged history of research. The size effect of traditional quasi-brittle materials can already be well described through the size effect model. However, there is still a lack of research on the size effect of strain-hardening cementitious composites (SHCC), a special type of fibre-reinforced concrete with macro-scale strain-hardening behaviour after first cracking. Being distinct from traditional quasi-brittle materials with softening nature, SHCC is thus expected to behave differently in terms of size effect. In this research, the structural size effect problem of SHCC is comprehensively studied by experimental investigation and theoretical analysis. Geometrically similar notched three-point bending specimens were tested in mode I and mixed mode I/II fracture condition. The whole-process of failure and matrix cracking zone around the main crack was captured with high resolution by digital image correlation technology. Experimental results showed that apparent fracture energy, nominal strength, structural ductility and fracture resistance curve are all structural size-dependent. The apparent fracture energy was shown to arise with specimen size within the tested range. This is related to large-scale pseudo yielding, i.e. enlargement of matrix cracking zone (like the yielding zone in metals) with increasing structural size. It thus provides an indirect method for the estimation of cohesive fracture energy of single crack with constitutive nature. Due to the scaled matrix cracking zone, an intermediate asymptote exists in the size effect curve of nominal strength, in addition to the plastic and LEFM asymptotes in the Bažant original size effect law. This resembles the recent finding of intermediate asymptote in plastic-hardening metal( Dönmez et al. 2023 ). The size-dependence of R-curve was also examined. Though size-dependent, the equivalent LEFM-based R-curves are shown to have three common stages reflecting different cracking processes. Based on experimental results, the size effect of fracture energy and nominal strength are finally modelled theoretically in the Bažant's framework of equivalence between energy release and fracture resistance.

Structure-fracture Relationships in Chocolate Systems

Combining fracture mechanics and rheology to investigate the impact of micro-aeration on chocolate oral processing

Study on the crystallization properties of several chocolates during tempering

Fracture Toughness And Microstructure Of Concrete At Early-Ages

A multiscale finite element analysis model for predicting the effect of micro-aeration on the fragmentation of chocolate during the first bite

Rate- and temperature-dependent ductile-to-brittle fracture transition: Experimental investigation and phase-field analysis for toffee

Frictional behaviour of molten chocolate as a function of fat content

Effect of Thermal and Mechanical Rejuvenation on Rheological Behavior of Chocolate

Measurement of molten chocolate friction under simulated tongue-palate kinematics: Effect of cocoa solids content and aeration

Insight into the mechanism of fracture properties modulated by microstructure in the myofibrillar protein and polysaccharide gel systems

The Influence of Temperatures on the Mechanical Properties and Fracture Behavior of Rocks under Mixed Mode I/II Loading

3 D In-situ XCT Image Based Mesoscale Fracture Modelling and Validation of Concrete Using Voxel Hexahedron Meshing and Damage Plasticity Model

Fracture behavior of PBX simulation subject to combined thermal and mechanical loads

3D meso-scale fracture modelling and validation of concrete based on in-situ X-ray Computed Tomography images using damage plasticity model

Proportioning optimization of transparent rock-like specimens with different fracture structures

Physical characterization of the milk chocolate using whey powder

Experimental and Theoretical Investigation of Size Effects on the Ductile/Brittle Fracture Toughness of A Pressure Steel

Structural size effect in the mode I and mixed mode I/II fracture of strain-hardening cementitious composites (SHCC)

Exploring the effects of structure and melting on sweetness in additively manufactured chocolate

Experimental Investigation of the Size Effects on the Fracture Toughness and Tearing Modulus