Growth, structure, and spectroscopic characteristics of a promising yellow laser crystal Dy:GdScO3

Fang Peng,Wenpeng Liu,Qingli Zhang,Jianqiao Luo,Dunlu Sun,Guihua Sun,Deming Zhang,Xiaofei Wang

DOI: https://doi.org/10.1016/j.jlumin.2018.04.034

IF: 3.6

2018-01-01

Journal of Luminescence

Abstract:High-quality Dy3+ doped GdScO3 (Dy:GdScO3) single crystal was grown successfully by the Czochralski method for the first time. The lattice parameters of the as-grown crystal were obtained by Rietveld refinement to its XRD patterns. The effective segregation coefficient of Dy3+ is calculated to be 0.68. The spectroscopic characteristics of Dy:GdScO3 are investigated, with special attention to the yellow emission that could be pumped directly by the rapidly developed blue GaN LD. The absorption cross section of Dy:GdScO3 at 453 nm is 1.8 × 10–21 cm2 and the FWHM of this absorption band is about 9 nm at 300 K. Meanwhile, Dy:GdScO3 exhibits strong yellow emission at 577 nm corresponding to the transition 4F9/2→6H13/2 with stimulated emission cross section of 4.1 × 10–21 cm2. The relatively long fluorescence lifetime (459 μs) and high radiative quantum efficiency of the 4F9/2 level indicate a high laser efficiency of Dy:GdScO3 crystal. All results suggest that Dy:GdScO3 crystal could be a promising candidate for yellow laser at 577 nm pumped by blue GaN LD.