Abstract:The selective catalytic reduction (SCR) is widely used for the NOx removal from the oxygen-rich exhaust gases of diesel passenger cars and trucks. SCR implies the reduction of NOx by NH3 originated from AdBlue, which is an aqueous solution of urea (32.5 wt.%) stored on-board of the vehicles. However, urea is not completely converted at low exhaust temperatures potentially resulting in by-products and deposits influencing the SCR performance. In this context, the present paper deals with the conversion of molten urea remaining from AdBlue evaporation. A novel reaction chamber equipped with laser Raman spectroscopy (LRS) for quantitative in situ analysis was constructed to examine the conversion of liquid urea as well as formation of side-products. Validation of the analytical set-up was made by ex situ tools including elemental analysis and infrared spectroscopy. The in situ LRS studies performed in diesel model exhaust between 150 and 170 °C evidenced accelerating conversion of the molten urea with increasing temperature, while substantial production of biuret occurred. Additionally, the influence of SCR catalysts such as V2O5/WO3/TiO2, TiO2, and Fe/BEA zeolite on the urea decomposition and by-product formation was evaluated. The in situ LRS investigations showed enhanced NH3 selectivity particularly for TiO2 associated with its pronounced hydrolysis activity in urea conversion. However, estimation of chemical and diffusion kinetics suggested that both hydrolysis and biuret production were strongly affected by mass transport of NH3 and H2O thus limiting the effect of the SCR catalysts upon the reaction of urea.

Low-Temperature Selective Catalytic Reduction of NOx with Urea Supported on Carbon Xerogels

Kinetics and Mechanism Study of Low-Temperature Selective Catalytic Reduction of NO with Urea Supported on Pitch-Based Spherical Activated Carbon

Selective catalytic reduction of no with urea supported on pitch-based spherical activated carbon at low temperatures

Design of a dual-bed catalyst system with microporous carbons and urea-supported mesoporous carbons for highly effective removal of NOx at room temperature

Removal of NO at low temperature and in the absence of ammonia over spherical activated carbon loaded with MnOx-CeO2 and urea

Low Temperature Selective Catalytic Reduction of NO and NO2 with NH3 over Activated Carbon-Supported Vanadium Oxide Catalyst

NO Catalytic Reduction on Urea-Loaded Ferromanganese Catalysts: Performance, Characterization, and Mechanism

[Reaction of NO with metal oxides and urea supported on activated carbons at low temperature]

Low-Temperature Scr of No with Nh3 over Activated Semi-Coke Composite-Supported Rare Earth Oxides

Laser Raman Spectroscopic Investigation on the Conversion of Molten Urea into NH3 for the Selective Catalytic Reduction of NOx in Oxygen-Rich Exhaust Gases

Low temperature selective catalytic reduction of nitric oxide with an activated carbon-supported zero-valent iron catalyst

Toward an Atomic-Level Understanding of the Catalytic Mechanism of Selective Catalytic Reduction of NO x with NH 3

Recent advance for NOx removal with carbonaceous material for low-temperature NH3-SCR reaction

Molecular-Level Insight into Selective Catalytic Reduction of NOx with NH3 to N2 over a Highly Efficient Bifunctional Va-MnOx Catalyst at Low Temperature

Research progress in carbon-based catalysts for NOx selective catalytic reduction at low temperature

Toward an Atomic-Level Understanding of the Catalytic Mechanism of Selective Catalytic Reduction of NOx with NH3

Cerium Oxide-Based Catalysts for Low-Temperature Selective Catalytic Reduction of NO x with NH 3 : A Review

Mn-Ce Oxide Nanoparticles Supported on Nitrogen-Doped Graphene for Low-Temperature Catalytic Reduction of NOx: De-Nitration Characteristics and Kinetics

Experimental Investigation on N2O Formation During the Selective Catalytic Reduction of NOx with NH3 over Cu-SSZ-13

Low-Temperature Removal of No by Spherical Activated Carbon Loaded with Mnox-Ceo2 and Melamine

Ammonia-Free Selective Catalytic Reduction of NO at Low Temperature on Melamine Impregnated MnOx–CeO2/Carbon Aerogels