Abstract:Both the cubic single crystals and the spherical polycrystals of cuprous oxides (Cu2O) were prepared by the reduction of aqueous CuSO4, with hydrazine as a reductant in the presence of different organic molecule additives, such as hexadecyltrimethyl ammonium bromide (CTAB), glucose (C6H12O6), ethylene glycol (C2H6O2), and glycerol (C3H8O3), at room temperature. It was found that the organic additives added had an important influence on the formation mechanism of the Cu2O particles and could lead to different microstructures of the resultant Cu2O crystallites. The addition of CTAB to the reaction solution could induce the formation of cubic Cu2O single crystals, while glucose resulted in the formation of spherical polycrystals. All the samples were characterized by X-ray powder diffraction and transmission electron microscope (TEM). TEM observations indicated that the nanosized primary particles formed immediately after the reactants were mixed, followed by the competition between diffusion of the reactive constituents and aggregation of the nanosized primary particles. In the presence of CTAB, the diffusion of the reactants was a major factor contributing to the single crystal morphology of the Cu2O products, while the aggregation of the primary nano-particles into polycrystallites prevailed when glucose existed in the reaction system.

Morphology Control of Cuprous Oxide Micro-and Nanoparticles by Polyol Method

Morphology Control Of Cuo Micro-Particles Using Zn2+ Ion And Ultrasonic Treatment

The Convenient Preparation of Porous CuO Via Copper Oxalate Precursor

A novel wet-chemical method of preparing highly monodispersed Cu2O nanoparticles

Microwave-Induced Polyol-Process Synthesis of Copper and Copper Oxide Nanocrystals with Controllable Morphology

Polyol synthesis and chemical conversion of Cu 2 O nanospheres

Preparation of Cuprous Oxide Particles of Different Crystallinity

Shape-Controlled Synthesis of Submicro-Sized Cuprous Oxide Octahedra

Preparation of Ultrafine Cu 2 O Powders with Different Morphologies from Cu(OH) 2 Gel

Morphology Control of Nanoscale PbS Particles in a Polyol Process

Morphology-Controlled Synthesis of Pbmoo4 Crystals by A Simple Sonochemical Method

Controllable growth of dendrite-like CuO nanostructures by ethylene glycol assisted hydrothermal process

One-Pot Fast Synthesis of Leaf-Like CuO Nanostructures and CuO/Ag Microspheres with Photocatalytic Application

Facile Synthesis of Leaf-like Cu(OH)2 and Its Conversion into CuO with Nanopores

Shape Effects of Cu<sub>2</sub>O Polyhedral Microcrystals on Photocatalytic Activity

Morphology-Controlled Synthesis of Magnetites with Nanoporous Structures and Excellent Magnetic Properties

Diameter and Aggregation Controlled Preparation by Solvothermal Synthesis of Ultra-small Particles CuFe$_2$O$_4$

Morphology-controlled Hydrothermal Synthesis and Growth Mechanism of Microcrystal Cu2O

A Simple Method for the Preparation of Cu2O with Different Morphologies in High Reaction Concentrations

Hetero-metal Cation Control of CuO Nanostructures and Their High Catalytic Performance for CO Oxidation.

Morphology control of Cu and Cu 2 O through electrodeposition on conducting polymer electrodes