Abstract:The alloying synergistic flame retardant effect was studied by using polyetherimide (PEI) and aluminum diethylphosphinate (ADP) for polyamide 6 (PA6), which can endow PA6 composites with excellent mechanical properties and flame retardancy simultaneously. On the one hand, because the molecular structures of PEI and PA6 are similar, adding PEI with PA6 can form PEI‐PA6 alloy by the hydrogen bond effect and nice homogeneous phase, which can endow PA6 composites with excellent mechanical properties. On the other hand, the test results of flame retardancy show that 9ADP/10PEI‐PA6 composite can obtain higher LOI value (LOI = 31%), and excellent flame retardant rating (UL94 V‐0) with 9%ADP and 10%PEI. From the results of cone calorimetry test, the pk‐HRR and THR of 9ADP/10PEI‐PA6 are reduced by 24.4% and 24.7%, respectively, compared to PA6, and higher char residue rate was obtained, which shows that ADP combined with PEI‐PA6 alloying exerts an excellent flame retardant synergistic effect. Through the study of flame retardant mechanism found that ADP works together with PEI can effectively increase the quenching effect in the gas phase, promote thermal stability, and delay the decomposition process of PA6 matrix during the combustion process. Meanwhile, it also increases the char yield to exert a synergistic effect in the condensed phase by ADP/PEI‐PA6. The residual char rate reached 36.6%, higher than neat PA6 about 4.6 wt.%. Thus, the alloying flame retardant method using ADP/PEI‐PA6 can endow PA6 with better flame retardancy and more excellent mechanical properties. Importantly, it provides a new direction for developing high‐performance halogen‐free flame retardant materials.

Semiaromatic Polyamide Poly(Hexamethylene Terephthalamide)-Co-Polycaprolactam: Thermal And Flame-Retardant Properties

Fascinating flame resistance of polycaprolactam copolymer containing d‐glucopyranose for melt‐spun flame retardant fibers

A phosphorus-containing flame retardant with thermal feature suitable for polyamide 6 and its filaments with enhanced anti-dripping performance

Synthesis and Characterization of a New Copolymer Consisting of Polyamide 1210 and Reactive Phosphorus-Nitrogen Flame-Retardant

A Strategy to Achieve the Inherently Flame-retardant PA56 by Copolymerization with DDP

Flame‐retardant polyamide 56 with high fire safety and good thermal performance

Corporate Governance for Crooks? The Case for Corporate Virtue

Polydimethylsiloxane Wrapped Aluminum Diethylphosphinate for Enhancing the Flame Retardancy of Polyamide 6

Preparation of high‐efficient flame retardant PA6 via DOPO‐ITA initiated ring‐opening polymerization of caprolactam

Alloying synergistic flame retardant effect improving fire resistance and mechanical properties of polyamide 6

Synthesis, Structures, and Properties of a New Pentaerythritol-Derived Flame Retardant Used in Polyamide 66

Halogen and Halogen-Free Flame Retarded Biologically-Based Polyamide with Markedly Suppressed Smoke and Toxic Gases Releases

Combustion and Thermal Properties of Polylactide with an Effective Phosphate-Containing Flame-Retardant Oligomer

Thermal Stabilities and Flame Retardancy of Polyamide 66 Prepared by In Situ Loading of Amino-Functionalized Polyphosphazene Microspheres

A Novel Phosphorous-Containing Polymeric Compatibilizer: Effective Reinforcement and Flame Retardancy in Glass Fiber Reinforced Polyamide 6 Composites

Combination of Corn Pith Fiber and Biobased Flame Retardant: A Novel Method toward Flame Retardancy, Thermal Stability, and Mechanical Properties of Polylactide

Polymer-type flame retardants based on a DOPO derivative for improving the flame retardancy of polyamide 6: Preparation, properties and flame retardancy mode of action

Fire-safe and tough semi-aromatic polyamide enabled by halloysite-based self-assembled microrods

Effect of the Flame Retardants and Glass Fiber on the Polyamide 66/Polyphenylene Oxide Composites

Memorial lecture: an evaluation of gastric acid secretion tests.

Preparation and Properties of Toughened/flame‐retardant PA6/glass‐fiber Composites Reinforced by Linear Polyphosphazene Elastomers