Large Polarization Switching and High-Temperature Magnetoelectric Coupling in Multiferroic GaFeO 3 Systems
Hui Wang,Yang Zhang,Koki Tachiyama,Zhaoyang Xia,Jinghong Fang,Qin Li,Guofeng Cheng,Yun Shi,Jianding Yu,Tsukasa Katayama,Shintaro Yasui,Mitsuru Itoh
DOI: https://doi.org/10.1021/acs.inorgchem.0c02855
IF: 4.6
2020-12-15
Inorganic Chemistry
Abstract:GaFeO<sub>3</sub>-type iron oxides are promising multiferroics due to the coexistence of large spontaneous magnetization and polarization near room temperature. However, the high leakage current and difficulties associated with synthesizing single crystals make it difficult to achieve two important features in the system: a large ferroelectric polarization switching and magnetoelectric coupling at a high-temperature region. Herein, we report successful achievement of these features by preparing high-quality Sc-doped GaFeO<sub>3</sub> single crystals (Sc<sub><i>x</i></sub>Ga<sub>1–<i>x</i>/2</sub>Fe<sub>1–<i>x</i>/2</sub>O<sub>3</sub> with <i>x</i> = 0–0.3) using the floating zone method. The <i>x</i> ≥ 0.05 crystals exhibit a leakage current 10<sup>4</sup> times lower than the <i>x</i> = 0 crystals, highlighting the importance of Sc doping. Because of the reduced leakage current, the Sc-doped crystals exhibit large ferroelectric polarization switching along the <i>c</i>-axis with a remanent polarization of 22–25 μC/cm<sup>2</sup>, which is close to the theoretically predicted polarization value of 25–28 μC/cm<sup>2</sup>. In addition, the Sc-doped crystals exhibit ferrimagnetism with magnetic anisotropy along the <i>a</i>-axis. Furthermore, a magnetic-field-induced modulation of polarization is observed in the <i>x</i> = 0.15 crystal even at a relatively high temperature, i.e., 100 K.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.inorgchem.0c02855?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.inorgchem.0c02855</a>.Single-crystal and Laue photographs, Arrhenius plots, polarization and current versus electric field curves, and element analysis by ICP (<a class="ext-link" href="/doi/suppl/10.1021/acs.inorgchem.0c02855/suppl_file/ic0c02855_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, inorganic & nuclear