Y3+/TiO2 Photocatalysts: Preparation via Ball Milling Method and Marine Aquaculture Wastewater Treatment
Li Chen,Wu Di,Zhang Da-Shuai,Wang Li-Li,Zhang Xiao-Peng,Liu Jian,Zhang Su-Min,Li Tian-Lue,Shi Zai-Feng,Lin Qiang
DOI: https://doi.org/10.11862/CJIC.2019.035
2019-01-01
Chinese journal of inorganic chemistry
Abstract:Y3+ modified TiO2 photocatalysts were prepared by ball milling method. The structures and properties of the photocatalysts were characterized by UV-visible diffuse reflectance spectroscopy (UV-Vis DRS), X-ray photoelectron spectroscopy (XPS), X-ray powder diffraction (XRD) and scanning electron microscopy (SEM). The photocatalytic activities were evaluated by the degradation of methylene blue (MB) aqueous solution under UV light, and the ball milling processes were optimized. Then Y3+/TiO2 photocatalysts prepared at the best conditions were coated on the plastic balls with different diameters. These balls were applied to treat shrimp wastewater under UV and visible light and CODCr (chemical oxygen demand) and 3D fluorescence spectroscopy were detected during the photocatalytic experiments. The results showed that when the molar ratio of Y3+ was 2%, milling time was 4 h, ball-to-powder weight ratio was 4:1 and milling rate was 500 r.min(-1), the reaction rate constant of MB degradation can reach up to 0.111 3 min(-1) which was 4.2 times as fast as pure TiO2. From the UV-Vis DRS, XPS, N-2 absorption-desorption, XRD, SEM results, the band gap of 2%Y3+/TiO2 decreased to 3.05 eV. All Y3+/TiO2 samples showed a redshift of absorption compared to pure TiO2 and it led to visible light absorption response. The content of surface oxygen vacancy had a significant increase and the BET specific area increased to 104 m(2) g(-1) Pure TiO2 and 2%Y3+/TiO2 were used as photocatalysts to treat shrimp wastewater, CODECr removal rates were 14.7% and 18.8% under visible light, respectively. Moreover, CODCr removal rates were 26.9% and 37.5% under UV light, respectively. The photocatalytic efficiencies of three types of plastic ball with diameters of 1, 2 and 3 cm were investigated. The results showed that the performance of 2 cm balls was best and COD removal rate was 38.5%.