Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

Photodecomposition of Methylene Blue by TiO2-mounted Diatomite

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Preparation and photocatalytic performance of TiO_2-mounted diatomite composites by a hydrothermal method

P-doped TiO_2 Immobilized Diatomite and Its Photocatalytic Performance under Visible Light

A Comparative Study of Different Diatomite-Supported Tio2 Composites and Their Photocatalytic Performance for Dye Degradation

Synthesis of Natural Porous Minerals Supported Tio2 Nanoparticles and Their Photocatalytic Performance Towards Rhodamine B Degradation

Microstructure and Photocatalytic Decomposition of Methylene Blue by Tio2-Mounted Halloysite, A Natural Tubular Mineral

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles

Integrated Nanostructures of TiO2/g-C3N4/Diatomite Based on Low-Grade Diatomite as Efficient Catalyst for Photocatalytic Degradation of Methylene Blue: Performance and Mechanism

Photocatalyst-coated Carbon Microtube Electrodes: Preparation and Characterization of Their Properties and Photocatalytic Degradation of Methylene Blue.

Photodegradation of an Azo Dye Using Immobilized Nanoparticles of TiO2 Supported by Natural Porous Mineral.

Photocatalytic Degradation of Methylene Blue in TiO2 Aqueous Suspensions Using Microwave Powered Electrodeless Discharge Lamps.

Synthesis of Nano-Tio2/diatomite Composite and Its Photocatalytic Degradation of Gaseous Formaldehyde

Photocatalytic Decomposition Of Mb Solution By Cnt/Tio(2) Composites Prepared From Mwcnt And Titanium Source

Preparation of TiO2-diatomite Composites by Ball-Milling and Its Photocatalytic Degradation of Methyl Orange

A high-stability silica-clay composite: synthesis, characterization and combination with TiO2 as a novel photocatalyst for Azo dye.

Rapid photocatalytic decolorization of methylene blue using high photon flux UV/TiO2/H2O2 process

Synthesis and Photocatalytic Property of SiO2/TiO2

Study on Influencing Factors of Photocatalytic Degradation of Methylene Blue by Nano-TiO2

Investigation of TiO2 Deposit on SiO2 Films: Synthesis, Characterization, and Efficiency for the Photocatalytic Discoloration of Methylene Blue in Aqueous Solution

Solar photocatalytic degradation of methylene blue in carbon-doped TiO2 nanoparticles suspension