Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

Photocatalytic degradation of dimethylamine in wastewater with nano-TiO;/diatomite

Preparation and characterization of nano-TiO;/diatomite photocatalyst for photocatalytic degradation of dimethylamine（DMA）

Synthesis of Nano-Tio2/diatomite Composite and Its Photocatalytic Degradation of Gaseous Formaldehyde

Integrated Nanostructures of TiO2/g-C3N4/Diatomite Based on Low-Grade Diatomite as Efficient Catalyst for Photocatalytic Degradation of Methylene Blue: Performance and Mechanism

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

TiO2 Nanoparticles Supported on PMMA Nanofibers for Photocatalytic Degradation of Methyl Orange

A Comparative Study of Different Diatomite-Supported Tio2 Composites and Their Photocatalytic Performance for Dye Degradation

A H2O2 Oxidation Approach to Ti3C2/TiO2 for Efficient Photocatalytic Removal of Distinct Organic Pollutants in Water.

Synthesis of Natural Porous Minerals Supported Tio2 Nanoparticles and Their Photocatalytic Performance Towards Rhodamine B Degradation

Preparation of TiO2/g-C3N4 composites and photocatalytic degradation unsymmetrical dimethylhydrazine waste water

P-doped TiO_2 Immobilized Diatomite and Its Photocatalytic Performance under Visible Light

Photocatalytic degradation of dyestuff wastewater under visible light irradiation using micron-sized mixed crystal TiO2 powders

Photocatalytic Degradation of 2,4-Dichlorophenol by TiO2 Intercalated Talc Nanocomposite

Photocatalytic Membrane Reactor for Degradation of Acid Red B Wastewater

Nano TiO2 Deposited on Crude Mineral and the Photoactivity to the Degradation of Chloroform

Photocatalytic mineralization of dimethoate in aqueous solutions using TiO2: Parameters and by-products analysis

Study on the Photocatalytic Degradation of Ammonia Nitrogen in Aquaculture Wastewater by Sn4+-Doped Nano-TiO2 under UV Irradiation

Defect-enhanced Photocatalytic Removal of Dimethylarsinic Acid over Mixed-Phase Mesoporous TiO 2

PHOTOCATALYTIC DEGRADATION OF PAM BY NANO-TITANIUM DIOXIDE

Preparation of Nano-Tio2/purified Diatomite Coating and Its Photocatalytic Properties of Formaldehyde Degradation

A novel method Hybrid Photo-electrocatalytic Oxidation for the treatment of 3,4-dimethyaniline wastewater: Degradation mechanism and synergistic effect