Investigation on Microstructures and Interfaces of NiC/Ti Neutron Multilayers

ZHANG Zhong,JIN Xin,LI Wen-bin,HUANG Qiu-shi,WANG Zhan-shan
DOI: https://doi.org/10.3788/ope.20172511.2859
2017-01-01
Optics and Precision Engineering
Abstract:NiC/Ti neutron supermirror plays a key role in improving the capability of neutron optics . In order to improve the performance of the neutron supermirror , a study in microstructures and interfaces of NiC/Ti multilayers with varied NiC layer thickness was presented . The thickness , interface roughness and crystalline state of NiC/Ti multilayers were represent by Grazing incidence X-ray reflectivity and X-ray diffraction , respectively . The study results indicate that the NiC-on-Ti interface roughness was almost constant except the thin NiC layer ,which has the thickness less than 2 .5 nm ,however the Ti-on-NiC interface roughness has relatively large changes . The NiC layers transferred from amorphous to polycrystal ,as the NiC layer thickness increase from 2 .5 nm to 5 .5 nm ,and both two interfaces and the size of Ni (111) crystalline grains almost kept constant as the NiC layer thickness continue to increase .This different variation between Ti-on-NiC and NiC-on-Ti interface roughness can be attributed to the microstructures changes resulting from varying NiC layer thickness .
What problem does this paper attempt to address?