Novel Hybrid p- and n-Type Organic Thermoelectric Materials Based on Mussel-Inspired Polydopamine
Yihan Wang,Siqi Wu,Qinjian Yin,Kai Du,Qiang Yin,Bo Jiang,Site Mo
DOI: https://doi.org/10.1021/acsami.1c01457
2021-05-11
Abstract:Mussel-inspired polydopamine (PDA) can serve as building blocks and interfaces in designing functional materials. Here, the use of PDA as an interlayer between polyaniline (PANi) and multidimensional carbon materials, such as graphene quantum dots (GQD), multiwalled carbon nanotubes (MWCNT), and graphene nanosheets (GNS), to improve the thermoelectric performance of p-type polymer-based materials has been reported. The introduction of PDA promotes the carrier mobility of GQD/PDA/PANi, CNT/PDA/PANi, and GNS/PDA/PANi ternary composites due to the superior adhesive property of PDA. An optimal conductivity of 4.98 × 10<sup>4</sup> S m<sup>–1</sup> and a power factor of 92.17 μW m<sup>–1</sup> K<sup>–2</sup> at 363 K are achieved in GNS/PDA/PANi, which are much higher than the values of GNS/PDA and GNS/PANi. More surprisingly, despite the fact that GQD/PDA, CNT/PDA, and GNS/PDA binary composites show p-type properties, the pyrolysis treatment of GQD/PDA, CNT/PDA, and GNS/PDA at 800 °C results in a gain in both the electrical conductivity and negative Seebeck coefficient of c-GQD/PDA, c-CNT/PDA, and c-GNS/PDA. The c-CNT/PDA composites possess the highest Seebeck value of −30.2 μV K<sup>–1</sup> and a maximum power factor value of 35.57 μW m<sup>–1</sup> K<sup>–2</sup>. Finally, a flexible thermoelectric generator with 24 thermoelectric units composed of GNS/PDA/PANi and c-CNT/PDA is demonstrated, which gives an output voltage of 52.8 mV at a temperature difference of 60 °C.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c01457?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c01457</a>.Thermal conductivity measurements and TE characterization; electrical conductivity and Seebeck coefficient of all the samples at 303, 333, and 363 K; TE properties of pristine GQD, CNT, and GNS at 363 K; FTIR spectra, XPS spectra, TEM images, and size distributions of GQD; appearance of GNS dispersion solution and GNS/PDA dispersion solution in water after ultrasonication; carrier mobility and carrier concentration of PANi-based composites at 363 K; PF and thermal conductivity of PDA and PDA-based composite materials at 363 K; PF and thermal conductivity of PANi-based binary composites at 363 K; digital photos of n-type composite films of bending 150 and 180° and after bending 180°; cross-sectional SEM images of n-type composite films of bending 180° and magnification times; digital photos showing bending of p-type composite films by 150 and 180° and after bending to 180°; cross-sectional SEM images showing the bending of p-type composite films by 180° and magnification times; and schematic diagram of the device configuration and the working principle of TEG (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c01457/suppl_file/am1c01457_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology