Abstract:In this paper, the corrosion behavior of three kinds of medium Cr low C steels in the simulated service environment of the transport pipeline was investigated through accelerated corrosion experiments, and the corrosion resistance mechanism of these experimental steels at different temperatures was investigated by electrochemical means. Finally, the reasons for the difference in corrosion behavior were analyzed from the grain boundary and surface Volta potential. The results show that as the temperature rose, the corrosion rate of the 5Cr specimen increased sharply and the corrosion type developed from slight general corrosion to severe general corrosion. The 7Cr specimen was less sensitive to temperature, and the type of corrosion changed from slight general corrosion to local corrosion. Finally, the 9Cr specimen was not sensitive to temperature, and the type of corrosion was always local corrosion. 5Cr steel could form a protective product film at 30°C. As the temperature rose, the protective ability of the product film decreased, and the matrix dissolved easily. The film of 7Cr and 9Cr samples had not yet precipitated and the matrix was difficult to dissolve at 30°C. However, the matrix dissolved easily at 50°C, and the product film had formed, which played a major role. At 70°C, the protective effect of the product film decreased, and the gap between the 7Cr and 9Cr samples began to appear. The increase of Cr content helped to refine grains and increased the proportion of low-angle grain boundaries. At the same time, the increase of Cr element helped to increase the maximum Volta potential of the experimental steel and increased the Volta potential difference. As a result, the test steel was shown to be resistant to uniform corrosion, but it also increased the risk of pitting corrosion.

Effects of Temperature on Corrosion of N80 and 3cr Steels in the Simulated $$\hbox {CO}_{2}$$ CO 2 Auxiliary Steam Drive Environment

Effects of Temperature on Corrosion of N80 and 3Cr Steels in the Simulated CO_2 Auxiliary Steam Drive Environment

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Corrosion Mechanism and Applicability Assessment of N80 and 9cr Steels in CO 2 Auxiliary Steam Drive

Effect of Temperature on CO_2 Corrosion Behavior of Tubular Steel

Investigation of the Effect of Temperature and Co2 Partial Pressure on Flow Corrosion of N80 Steel in Formation Water Environment

Influence of temperature on corrosion behavior of N80 steel in CO2/O2 co-existing environment

Effects of CO2 Gassy-Supercritical Phase Transition on Corrosion Behaviors of Carbon Steels in Saturated Vapor Environment

Effect of Temperature on Scales of Carbon Dioxide Corrosion Products

Effect of Temperature on CO2/H2S Corrosion Rate of Oil Tube Steels

Effect of Temperature on Microstructure and Mechanical Properties of CO_2 Corrosion Scale on N80 Sreel

Effect of Temperature on CO2 Corrosion Scales of Tubular Steels

Effect of Temperature and Pressure on CO2/H2S Corrosion Rate of N80 Steel

Effect of Temperature and Composition on Corrosion Behavior of Medium Cr Steel in a Salt Solution Containing CO2

Influence of Temperature on Corrosion Behavior of N80 Steel in Multiple Thermal Fluid Environment

Effect of Temperature on Corrosion Behavior of T95 Steel in H2 S/CO2 Environment

Effect Of Temperature On Corrosion Behaviour Of X70 Steel In High Pressure Co2/So2/O-2/H2o Environments

Corrosion Behavior of Oil Tubular Goods Under Supercritical CO2 Conditions in High Temperature and High Pressure Sour Gas Wells

Study on Corrosion of Cr-containing Steel under Different CO2 Partial Pressures at High Temperatures

Effect of Temperature on Corrosion Behavior and Mechanism of S135 and G105 Steels in CO2/H2S Coexisting System

Effect of Temperature on H<sub>2</sub>S/CO<sub>2</sub> Corrosion Behaviors of P110-3Cr Steel