Two-dimensional silica enhanced solid polymer electrolyte for lithium metal batteries
Zhihong Luo,Weiyong Li,Chong Guo,Ya Song,Mingxia Zhou,Yan Shi,Jing Xu,Long Li,Bin Shi,Quansheng Ouyang,Jiao-Jing Shao,Guangmin Zhou,Jiaojing Shao
DOI: https://doi.org/10.1016/j.partic.2023.04.002
IF: 3.5
2023-04-27
Particuology
Abstract:Solid polymer electrolytes (SPEs) are promising substitutes for current flammable liquid electrolytes to achieve high-safety and high-energy-density lithium metal batteries. Polyethylene oxide (PEO) based solid polymer electrolytes have attracted increasing attention because of their excellent flexibility, manufacturability, light weight, and low-cost processing, while they often suffer from low ionic conductivity at room temperature, low lithium transference number and unsatisfactory interfacial resistance, which largely restrain their practical application. Herein, two-dimensional holey silica nanosheets (2D-HSN) as the fillers, together with LiNO 3 as the electrolyte additive, are introduced in a PEO/poly(vinylidene fiuoride-co-hexafluoropropylene) (PVDF-HFP) blended polymer matrix to obtain a SPE. The incorporation of HSN filler creates supplementary channels for lithium ion migration and lowers the crystallinity of the polymer, thereby facilitating the movement of lithium ions. The HSN-based SPE demonstrates higher ionic conductivity up to 3.7 × 10 −4 S cm −1 at 30 °C, larger Li + transference number close to 0.34, and more stable lithium plating/stripping than that without the fillers, and HSN can promote the formation of more stable solid electrolyte interphase (SEI) layer. The as-assembled LiFePO 4 ||Li batteries deliver a high specific capacity of 159 mA h g −1 with the capacity retention of 95.5% after 200 cycles at 30 °C, as well as superior rate performance and cycling stability compared to that using the blank SPE.
materials science, multidisciplinary,engineering, chemical