Abstract:Traditional ceramic separation membranes, which are fabricated by applying colloidal suspensions of metal hydroxides to porous supports, tend to suffer from pinholes and cracks that seriously affect their quality. Other intrinsic problems for these membranes include dramatic losses of flux when the pore sizes are reduced to enhance selectivity and dead-end pores that make do contribution to filtration. In this work, we propose a new strategy for addressing these problems by constructing a hierarchically structured separation layer on a porous substrate using large titanate nanofibers and smaller boehmite nanofibers. The nanofibers are able to divide large voids into smaller ones without forming dead-end pores and with the minimum reduction of the total void volume. The separation layer of nanofibers has a porosity of over 70% of its volume, whereas the separation layer in conventional ceramic membranes has a porosity below 36% and inevitably includes dead-end pores that make no contribution to the flux. This radical change in membrane texture greatly enhances. membrane performance. The resulting membranes were able to filter out 95.3% of 60-nm particles from a 0.01 wt % latex while maintaining a relatively high flux of between 800 and 1000 L/m(2).h, under a low driving pressure (20 kPa). Such flow rates are orders of magnitude greater than those of conventional membranes with equal selectivity. Moreover, the flux was stable at approximately 800 L/m(2).h with a selectivity of more than 95%, even after six repeated runs of filtration and calcination. Use of different supports, either porous glass or porous alumina, had no substantial effect on the performance of the membranes; thus, it is possible to construct the membranes from a variety of supports without compromising functionality. The Darcy equation satisfactorily describes the correlation between the filtration flux and the structural parameters of the new membranes. The assembly of nanofiber meshes to combine high flux with excellent selectivity is an exciting new direction in membrane fabrication.

Freeze-casting of Alumina Ultra-Filtration Membranes with Good Performance for Anionic Dye Separation

Preparation and Modification of Ceramic Membrane and Its Application in Oil/Water Wastewater Treatment

Preparation and Application of Flat-Plate Ceramic Ultrafiltration Membrane with High-Performance by Spray-Dip Coating Method

Preparation of a new ceramic microfiltration membrane with a separation layer of attapulgite nanofibers

One-step fabrication of asymmetric alumina ceramic membranes with tunable pore parameters for oil-water separation

Integrated preparation of alumina microfiltration membrane with super permeability and high selectivity

High-flux ceramic membrane derived from UV-curable slurry for efficient separation of nanoparticles suspension

The preparation and performance of alumina ultrafiltration membrane

Spheroidization of Low-Cost Alumina Powders for the Preparation of High-Flux Flat-Sheet Ceramic Membranes

Preparation of Alumina Membranes Comprising a Thin Separation Layer and a Support with Straight Open Pores for Water Desalination

Melded Ceramic Membranes: A Novel Fabrication Method for Ultrathin Alumina Membranes of High Performance

A Simple Method for Fabrication of Highly Ordered Porous Alpha-Alumina Ceramic Membranes

High-Flux Ceramic Membranes with a Nanomesh of Metal Oxide Nanofibers

Preparation of Alumina Hollow Fiber Ultrafiltration Membrane by Filtering Coating

Preparation of high permeable alumina ceramic membrane with good separation performance via UV curing technique

Preparation of α-alumina/γ-alumina/γ-alumina-titania ceramic composite membrane for chloride ion removal

Preparation of high-permeance ceramic microfiltration membranes using a pore-sealing method

Nanoscale Phase Transition Seeds-Assisted Low Temperature Preparation of Α-Al2o3 Ultrafiltration Membrane

Preparation and mechanism analysis of high performance ceramic membrane by spray coating

One-step Coating and Characterization of Α-Al2o3 Microfiltration Membrane

Fabrication of a Charged PDA/PEI/Al2O3 Composite Nanofiltration Membrane for Desalination at High Temperatures