Abstract:Geopolymer is a potential substitute for high-emission cement production . Therefore, the use of fly ash with high emission as a geopolymer is an environmentally friendly and inexpensive direction. However, fly ash (FA) is a high amorphous precursor with low pozzolanic reactivity making it difficult to be activated by calcium hydroxide. In this study, the coupling of wet-milling mechanical force and calcium hydroxide was used to prepare high-performance alkaline calcium activated geopolymers. Two kinds of FA slurries with different particle sizes of D 50 = 2.96 μm and 14.2 μm were prepared, activated by calcium hydroxide (CH) with the content of 4%, 11% and 19%. Results indicated that the increase of calcium hydroxide content was beneficial to developing strength, effectively improving the chloride resistance, compacting the microstructure, but increasing the autogenous shrinkage of the geopolymers. These improvements are especially apparent in the wet-milled fly ash geopolymers (WFA) due to the pre-depolymerization implemented by wet-milled mechanical forces, and coupled with the activation effect of CH to improve the depolymerization efficiency and condensation reaction. The compressive strength of WF-CH-19 was three times higher than that of FA-CH-19, reaching 29.3 MPa at 28 d, and the compressive strength growth of WF-CH-11 even reached 591.67% at 1 d. Meanwhile, the main chain length (MCL) and Al/Si of calcium silicate hydrates were clearly improved, and pore structure was significantly refined with capillary pore increased from 29.79% to 89.23%. In addition, FA and WFA geopolymers have significant advantages over Portland cement in the environmental impact indicators such as E-energy and E-CO 2 .

Mechanical and microstructural characterization of geopolymers derived from red mud and fly ashes

Mechanical Properties of Geopolymers Synthesized from Fly Ash and Red Mud under Ambient Conditions

Synthesis, Characterization, and Mechanical Properties of Red Mud–Based Geopolymers

A high-strength red mud–fly ash geopolymer and the implications of curing temperature

The Strength and Microstructure of Two Geopolymers Derived from Metakaolin and Red Mud-Fly Ash Admixture: A Comparative Study

Designing low-carbon fly ash based geopolymer with red mud and blast furnace slag wastes: Performance, microstructure and mechanism

Synthesis Factors Affecting Mechanical Properties, Microstructure, and Chemical Composition of Red Mud–fly Ash Based Geopolymers

Preparation and curing method of red mud-calcium carbide slag synergistically activated fly ash-ground granulated blast furnace slag based eco-friendly geopolymer

Geopolymerization of Red Mud and Rice Husk Ash and Potentials of the Resulting Geopolymeric Products for Civil Infrastructure Applications

Utilization of municipal solid waste incineration fly ash with red mud-carbide slag for eco-friendly geopolymer preparation

Synthesis And Characterization Of Geopolymers From Coal Gangue, Fly Ash And Red Mud

Synthesis of Geopolymers Using Municipal Solid Waste Incineration Fly Ash and Construction and Demolition Waste: Mechanical and Thermal Activation

Synthesis and Characterization of Red Mud and Rice Husk Ash-Based Geopolymer Composites

Mechanical properties and microstructure of red mud-coal metakaolin geopolymer concrete based on orthogonal tests

Preparation and Research on Mechanical Properties of Eco-Friendly Geopolymer Grouting Cementitious Materials Based on Industrial Solid Wastes

Investigation on red mud and fly ash-based geopolymer: Quantification of reactive aluminosilicate and derivation of effective Si/Al molar ratio

Compressive strength of fly ash based geopolymer utilizing waste completely decomposed granite

Interfacial Behavior of Slag, Fly Ash, and Red Mud-Based Geopolymer Mortar with Concrete Substrate: Mechanical Properties and Microstructure

Alkali-hydrothermal activation of tailings with red mud as a supplementary alkali source to synthesize one-part geopolymer

Effect of composite activators on mechanical properties, hydration activity and microstructure of red mud-based geopolymer

An efficient approach for sustainable fly ash geopolymer by coupled activation of wet-milling mechanical force and calcium hydroxide