Abstract:FePt films being with high coercivity, large energy product and corrosion resistance, are highly potential in applications such as MEMs, ultra-high density magnetic recording, and others. Much attention has been paid to the preparation of high quality films at substrate/annealing temperatures as low as possible to accommodate processing adopted in the manufacture of MEMs or sensors. In this study FexPt1-x thin films were deposited by DC magnetron sputtering onto Si(100) and CrMo-seeded glass substrates at a substrate temperature (Ts) 30 to 600 degreesC with or without further post-annealing. Optimum magnetic properties of our studied films were obtained at the Fe53Pt47 composition as-deposited at Ts 300 degreesC. The in-plane coercivity (Hc) is 8 kOe for as-deposited films on both Si(100) and glass, substrates. The films on Si(100) showed a maximum magnetization (M2T) and a maximum energy product of 950 emu/cm(3) and 15.8 MGOe, respectively. The squareness ratio (M-r/M-s) of the as-deposited FePt films on glass substrate increases with increasing Ts. Minor hysteresis loops reveal that domain-wall-pinning dominates the magnetic hardening of the FePt films. Post annealing at 400 degreesC substantially enhances coercivity and energy product for the Fe53Pt47 films on glass substrate. Ordering parameters were studied by XRD and quantitatively correlated to magnetic properties.

Structure and Magnetic Properties of Graded (001)-Oriented FePt Films Prepared by Magnetron Sputtering and Rapid Thermal Annealing

Structural and magnetic properties of nanostructured FePt/MgO granular films

Improvement of magnetic property of L10‐FePt film by FePt∕Au multilayer structure

Effect of Annealing on the Microstructures and the Magnetic Properties of [fe/pt]16 Multilayers on MgO (001) Substrates

Magnetic Anisotropy of L10-FePt Film on (001) LaAlO3

Reducing the Writing Field of L1-FePt by Graded Order Parameter

Enhancement of Magnetic Anisotropy for L10-(0 0 1) FePt Films Grown on SrTiO3 Substrate

Magnetic and Magneto-Optical Properties of Perpendicularly C-Axis Orientated FePt Thin Films

Microstructure and Magnetic Properties of Rapidly Annealed FePt (001) and FePt–MgO (001) Films

Structural and magnetic properties of FePt films grown on Cr 1-x Mo x underlayers

Structural and Magnetic Properties of FePt Films Grown on Cr1-xMox Underlayers

Annealing Effect on the Fe/Pt Multilayers Grown on Al2o3 (0001) Substrates

Epitaxial L10 FePt Films on SrTiO3 (100) by Sputtering

Enhanced Structural And Magnetic Ordering Of Fept/Mn-Oxide Bilayers By Ion-Beam Bombardment And Annealing

Low-Temperature In-Situ Growth Of High-Coercivity Fe-Pt Films

Magnetic and Magneto-Optical Properties of Co-Sputtering Fept Films

High Coercivity and Small Grains of FePt Films Annealed in High Magnetic Fields

Microstructural and magnetic properties of L1 0 FePt C (0 0 1) textured nanocomposite films grown on different intermediate layers

Epitaxial L10 FePt films on SrTiO3 (1 0 0) by sputtering

Microstructure and magnetic properties of FePt thin films for the coating of magnetic force microscopy tips

L10 FePt films epitaxially grown on MgO substrates with or without a Cr underlayer