Abstract:Casting experiments were carried out on Al–7Si using different additions of rare earth Ce at a reaction temperature of 1200 K. Based on the ternary phase diagram of Al–Si–Ce, the effects of rare earth Ce on the α-Al grain refinement, the mechanism of the eutectic Si phase modification, as well as on the mechanical properties and fracture morphology of the alloy were investigated. The results show that the addition of rare earth Ce generates a Ce-containing phase inside the alloy, which becomes a heterogeneous core of eutectic Si and changes the nucleation conditions of eutectic Si. The mechanical properties of the alloy were optimal when the Ce addition was 0.2 wt.%, and the defect porosity and average pore area were minimized. Ce-containing phases were found at fracture cracks, and these Ce-containing phases were deviated and aggregated at grain boundaries, which induced defects to be generated, and microcracks were easily produced during plastic deformation, which ultimately led to the fracture of the alloy. According to the growth kinetic relationship, due to the difference of different atomic radii, the inter-atomic forces lead to different nucleation densities of grains. With the generation of Ce-containing phases at the interfaces, the eutectic Si changes its growth direction and grows towards a 70° angle to the original direction with a tighter atomic ordering sequence of the stacking, and more twinned Si is generated and gradually stacked up at the interfaces, which directly alters the morphology of the eutectic Si.

Effect of Al-and Ce-content on Microstructure of Mg-Al Magnesium Alloys

Effect of Ce Content on the Microstructure of Semisolid Mg-10Al Alloy

Effect of Ce Content on the Microstructure and Mechanical Properties of Squeeze-Cast Al–5Mg-2.2Si-0.6Mn Alloys

Effects of Mg, Ce and Cu Content on Microstructure of 2D70 Aluminum Alloy

Effect of Ce Content on the Microstructure and Mechanical Properties of Al-Cu-Li Alloy

Effect of Ce Addition on the Microstructure, Thermal Conductivity and Mechanical Properties of Mg–0.5Mn Alloys

Effect of Micro-alloyed Ce on the Microstructure and Mechanical Properties of Mg-Gd-Zr Alloy

Effects of Ce content on the modification of Mg2Si phase in Mg-5Al-2Si alloy

Effect of cerium alloying on microstructure, texture and mechanical properties of magnesium during cold-rolling process

Effect of Cerium on Microstructures and Mechanical Properties of Az61 Wrought Magnesium Alloy

Effect of Ce Addition on Modifying the Microstructure and Achieving a High Elongation with a Relatively High Strength of As-Extruded AZ80 Magnesium Alloy

Effect of Fe, Mn, Ce on the Microstructure and Mechanical Properties of Al-Mg and Al-Mg-Si Die Casting Alloys

Effect of Ce Microalloying on Microstructure and Mechanical Properties of Extruded Mg–10Gd–0.5Zr Alloy

Effect of Rare Earth Ce Addition on the Microstructure and Mechanical Properties of an Al–Cu–Mg–Ag Alloy

Effect of the addition of cerium on the microstructure evolution and thermal expansion properties of cast Al-Cu-Fe alloy

Effect of rare earth Ce on the microstructure and mechanical properties of cast Al–7Si alloys

Effect of Sm and Ce content on microstructure and mechanical property of newly developed Mg-Sm-Ce-Mn based alloy

Effect of Ce Addition on Microstructure, Thermal Conductivity, and Mechanical Properties of As-Cast and As-Extruded Mg–3Sn Alloys

Tailoring the microstructure and enhancing the corrosion resistance of extruded dilute Mg-0.6Al-0.5Mn-0.25Ca alloy by adding trace Ce

Effect of Ce on the Microstructure and Corrosion Resistance of Al-5Mg-3Zn-1Cu Alloy

A comparative study on the effect of 0.5 wt% Ca or Ce on the microstructure, texture, and mechanical properties of the hot-rolled Mg-4Li alloy