Abstract:Ordered mesoporous carbons with semi-graphitized walls (OMCs-SGW) were successfully obtained by in situ silica-confined thermal decomposition of methane at low temperatures (800–1000 °C). This novel method, adopting ordered mesoporous silicas (OMSs) as hard templates, impregnating OMSs with small amounts of group VIII metal (Fe, Co, Ni) nitrates as catalysts, combining pore infiltration and carbonization/graphitization processes into a single step, provides an efficient way for the synthesis of OMCs-SGW. Methane, a special carbon precursor with small molecular size, is adopted because it allows complete penetration, and full carbon deposition inside the mesopores and is an easy graphitization process at low temperature assisted by catalysts. Two mesoporous silica materials, SBA-15 with hexagonal structure ( p6m ) and KIT-6 with cubic bicontinuous structure ( Ia3d ), were used as hard templates. SAXS patterns and TEM results show that the obtained carbon materials are faithfully replicated from the mesostructures of silica templates. Their pore walls are semi-graphitized and little structural shrinkage and negligible micropores are observed. The textural, structural properties and degree of graphitization of the OMCs-SGW can be conveniently tuned by controlling the temperature, namely, higher temperatures (e.g. 1000 °C) lead to products with more ordered and graphitized frameworks, but lower surface areas and pore volumes (about 390 m 2 /g and 0.45 cm 3 /g), while lower temperature (800 °C) results in products with less ordered and graphitized structures, but very high surface areas and pore volumes (up to 1200 m 2 /g and 2.08 cm 3 /g). OMCs-SGW can also be synthesized without catalysts. They have higher surface areas and pore volumes but much lower graphitized structures than the counterparts synthesized with catalysts. These OMCs-SGW show good hydrogen uptake capabilities (up to ~2 wt% at 10 bar and 77 K).

Synthesis of Freestanding Amorphous Giant Carbon Tubes with Outstanding Oil Sorption and Water Oxidation Properties

Water-Assisted Preparation of High-Purity Semiconducting (14,4) Carbon Nanotubes

Growth Of High-Quality Single-Wall Carbon Nanotubes Without Amorphous Carbon Formation

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

Structurally Designed Synthesis of Mechanically Stable Poly(benzoxazine-co-resol)-Based Porous Carbon Monoliths and Their Application As High-Performance CO2 Capture Sorbents

Catalyst-Free in Situ Carbon Nanotube Growth in Confined Space Via High Temperature Gradient

Vapor–Dissociation–Solid Growth of Three-Dimensional Graphite-like Capsules with Delicate Morphology and Atomic-level Thickness Control

Quartz Nonadherent and Clean Exfoliation of the Heteroatom-Doped Bulk Carbon Nanotubes Array

Surfactant‐Free Synthesis of Crystalline Mesoporous Metal Oxides by a Seeds/ NaCl‐Mediated Growth Strategy

High-Density Growth of Single-Wall Carbon Nanotubes on Silicon by Fabrication of Nanosized Catalyst Thin Films

Synthesis of Ordered Mesoporous Carbon Materials with Semi-Graphitized Walls via Direct In-situ Silica-Confined Thermal Decomposition of CH 4 and Their Hydrogen Storage Properties

Interface Tension-Induced Synthesis of Monodispersed Mesoporous Carbon Hemispheres

Mechanistic Insight into the Synthesis and Morphological Evolution of Superhydrophobic Silica Nanotubes

Molecular Engineering toward High‐Crystallinity Yet High‐Surface‐Area Porous Carbon Nanosheets for Enhanced Electrocatalytic Oxygen Reduction

Synthesis of Graphdiyne Hollow Spheres and Multiwalled Nanotubes and Applications in Water Purification and Raman Sensing

Growing pillars of densely packed carbon nanotubes on Ni-coated silica

Facile synthesis of highly graphitized porous carbon monoliths with a balance on crystallization and pore-structure

The Synthesis of Porous Materials with Macroscopically Oriented Mesopores Interconnected by Branched Mesopores

Controllable synthesis of porous tubular carbon by a Ag + -ligand-assisted Stöber-silica/carbon assembly process

Facile Synthesis of Hierarchically Porous Metal-TiO2/graphitic Carbon Microspheres by Colloidal Crystal Templating Method

Low-temperature organic solvent-based synthesis of amorphous porous carbon nanoparticles with high specific surface area at ambient atmosphere