Abstract:Tungsten carbide (WC) and Tungsten carbonitride (WCN) coatings are deposited by reactive high-power impulse magnetron sputtering (HiPIMS) with various nitrogen gas flow rates. The characteristics of discharge current and plasma optical emission of HiPIMS are recorded by oscilloscope (OSC) and optical emission spectroscopy (OES). The results exhibit that the peak discharge currents and the intensities of optical emission spectra lines are significantly influenced by the addition of nitrogen. The elemental concentration, microstructure, mechanical and tribological properties in ambient temperature and high temperature of deposited coatings are investigated by a wide variety of techniques such as energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), nano-indentation measurement, scanning electron microscope (SEM), atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS), and ball-on-disk tribometer. The results show that WC/WCN coatings with different microstructures, mechanical properties and tribological properties have been produced by controlling the flow rate of N2. Meanwhile, with the N2 flow rate increasing from 0 sccm to 24 sccm, (101) diffraction peak shifts to low angle. Moreover, (102) and (110) peaks’ intensities and the angle of (101) peak of β-W2C phase of the deposited WCN coatings decrease and disappear, and the average grain size decreases from 8.9 nm to 6.4 nm. XPS results show that the intensities of C=N, W–N, W–C–N, and N–O peaks increase while the intensity of C–W peak decreases. The deposited coatings change from slight columnar type to a typically dense and featureless structure, and the surface roughness decreases from Ra 11.6 nm at 0 sccm to Ra 5.7 nm at 24 sccm. The variation of nitrogen flow also plays a role in the mechanical properties of the coatings. It is found that the maximum hardness and elastic modulus of 35.6 GPa and 476.5 GPa appear at 16 sccm N2 flow rate. The results of wear tests demonstrate the addition of nitrogen slightly deteriorates tribological properties at room temperature (25 °C), but can remarkably improve tribological properties at high temperature (400 °C) of WC/WCN coatings deposited with an appropriate flow rate of nitrogen.

Significant Friction Reduction of High-Intensity Pulsed Ion Beam Irradiated WC-Ni Against Graphite under Water Lubrication

The Effect of Irradiation Parameters of High-Intensity Pulsed Ion Beam on Tribology Performance of YWN8 Cemented Carbides

Wear Behavior of WC-Ni Sliding Against Graphite under Water Lubrication

Friction Performance of Wc-Co Coating with Lithium Grease and Water Lubrication

Preparation and Tribological Properties of WS2 Solid Lubricating Coating with Dense Structure Using HiPIMS

Ultralow Friction Between Cemented Carbide and Graphite in Water Using Three-Step Ring-on-ring Friction Test

Friction and wear characteristics of WC-10Co-4Cr/Si 3N 4 tribopair lubricated under silt-laden water

The friction and wear of electroless Ni–P matrix with PTFE and/or SiC particles composite

Influences of Nitrogen Flow Rate on Microstructure, Mechanical and Tribological Properties of WCN Coatings Deposited by HiPIMS

Friction and wear properties of CrSiCN coatings with low carbon content as sliding against SiC and steel balls in water

Structural, mechanical and tribological properties of WCTiN coatings produced by HiPIMS

Preparation of WC/Ni Flexible Cloth Coating by Vacuum Brazing

Effect of Nano-Crystals at Surfaces Induced by Ion Beam Irradiation on the Tribological Behaviour in Microforming

Tribological Properties of Hard TiB2 Thin Films Prepared at Low Temperatures Using HiPIMS

Microstructure and tribological properties of Ni-based self-lubricating coating

Study on the friction and wear properties of nickel-based-WC-10Ni composite coatings prepared on the surface of TC4 titanium alloy

Friction and Wear Behavior of Electroless Wear-Resistant and Self-Lubricating Ni-P Composite Coatings

WC-Ni-Cr-based Self-Lubricating Composites Fabricated by Pulsed Electric Current Sintering with Addition of WS2 Solid Lubricant

Tribological characteristics of WC-Cr3C2-Ni cermet coatings under different wear parameters

Tribochemical Behavior of Si 3 N 4 –hbn Ceramic Materials with Water Lubrication

Microstructure and Tribological Properties of Multilayered ZrCrW(C)N Coatings Fabricated by Cathodic Vacuum-Arc Deposition