Investigation on Ce3+ Luminescence from Different Crystallographic Sites, Self Energy Transfer and Abnormal Thermal Stability of Nitrided Ba9Y2Si6O24: Ce3+ Phosphor for W-LEDs

Bing Peng,Kaixin Song,Huawen Wang,Shuangshuang Zhang,Weitao Su,Zhiqun Cheng

DOI: https://doi.org/10.1016/j.ceramint.2018.01.061

IF: 5.532

2018-01-01

Ceramics International

Abstract:The nitrided Ba9Y2Si6O24:Ce3+ phosphors were prepared by the conventional high temperature solid state reaction. The site occupancy of Ce3+ ionic and its luminescent characteristics were clearly analyzed in Ba9Y2Si6O24 hosts by Rietveld refinement of XRD data, PL & PLE spectra analyses, as well as the first principle calculation. Compared with Ba9Y2Si6O24: Ce3+ phosphors, p-d orbital hybridization between N3--p and Ce3+ -d orbital after the nitridation leads to red shifts of Ce-(Ba)(1)(3+) and Ce-(Ba(2,3))(3+) lattice ionic emission peaks. Meanwhile, the self-energy transfer was pointed from Ce-(Ba)(3+) lattice sites to Ce-(y)(3+) lattice sites by the analysis of PL&PLE spectra and CIE chromaticity diagram. By optimizing the N3- concentration, there exists abnormal outstanding thermal-stability of nitrided Ba9Y2Si6O24: Ce3+ phosphors, its emission intensities at 453 K are higher than that of room temperature (293 K). The whole photoluminescent properties of nitrided Ba9Y2Si6O24: Ce3+ phosphors were superior to that of Ba9Y2Si6O24: Ce3+ phosphors without nitridation. It hints the nitrided Ba9Y2Si6O24: Ce3+ phosphors to be a promising candidate as a green phosphor for W-LEDs, and the nitridation technology might be an important feasible strategy to enhance and develop the luminescent properties for silicate and aluminates based phosphors.