Y2Si4N6C:Ce3+ carbidonitride green-yellow phosphors: novel synthesis, photoluminescence properties, and applications

Jieqiong Wan,Qian Liu,Guanghui Liu,Zhenzhen Zhou,Rong-Jun Xie
DOI: https://doi.org/10.1039/c7tc01010a
IF: 6.4
2017-01-01
Journal of Materials Chemistry C
Abstract:The Y2Si4N6C:Ce3+ carbidonitride phosphor has been successfully synthesized via a novel acid-driven carbonization and carbothermal reduction nitridation method (ADC-CRN). This novel approach for Y2Si4N6C:Ce3+ promises lower heating temperature and shorter heating time than classical methods, indicative of a cost-effective and facile way to search for new silicon-based carbidonitrides. In contrast to Ce3+ activated (oxy) nitrides showing blue-green emissions, Y2Si4N6C:Ce3+ exhibits an individual green-yellowish emission band centered at 550 nm which is ascribed to the incorporation of highly covalent C4- into the host lattice. The sp(3) hybrid C4- was identified through high resolution electron energy loss spectroscopy analysis (EELS). Direct evidence for sole substitution of Ce3+ for Y3+ in Y2Si4N6C is represented for the first time using electron paramagnetic resonance (EPR) spectra. The red shift induced by the increasing Ce3+ content in Y2Si4N6C is reasonably deduced by the energy transfer model of intra-Ce3+ and inter-Ce3+ ions. A pc-w-LED packaging was fabricated via a combination of the yellow Y2Si4N6C:Ce3+ and blue La2Si4N6C:Ce3+ phosphors prepared using a 365 nm n-UV chip. The w-LED device shows a good color rendering index (R-a), CIE chromaticity coordinates and correlated color temperature (CCT) of 83.8, (0.3258, 0.3314) and 5819 K, respectively. These results suggest that Y2Si4N6C: Ce3+ has great potential for use in UV-LED-driven white emitting diodes.
What problem does this paper attempt to address?